CFB副產石灰?配爐石粉製作混凝土成效研究; lime CFB byproduct powder doped with blast furnace slag to product of concrete on the Effectiveness Research

NCU Institutional Repository > 工學院 > 土木工程研究所 > 博碩士論文 > Item 987654321/1353

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/1353

题名:	CFB副產石灰?配爐石粉製作混凝土成效研究;lime CFB byproduct powder doped with blast furnace slag to product of concrete on the Effectiveness Research
作者:	汪翊鐙;I-Teng Wang
贡献者:	土木工程研究所
关键词:	CFB副產石灰;抗壓強度;凝結時間;CFB byproduct lime;setting time;compressive strength
日期:	2009-07-03
上传时间:	2009-09-18 17:28:08 (UTC+8)
出版者:	國立中央大學圖書館
摘要:	高溫循環式流體化床發電鍋爐(Circulating Fluidized Bed Boiler，簡稱CFB)以燃燒石油焦來發電，同時避免燃燒後高含硫量之石油焦產生硫氧化物過量排放，故添加石灰石進行脫硫，所產生之副產物，即為CFB副產石灰。本研究利用水泥-爐石粉膠結系統添加CFB副產石灰為激發效果之技術發展，一方面對CFB副產石灰做品質穩定性之檢驗，做為每批CFB副產石灰摻配爐石粉製作混凝土之可行性判斷依據，並建立資料庫。另外，針對添加CFB飛灰於水泥-爐石粉系統所拌製之混凝土應用，進行現場實廠試拌及現地澆注，同時觀測現地混凝土之使用成效，以及實驗室內之CFB飛灰混凝土耐久性測試，以掌握添加CFB副產石灰所製成混凝土之長期應用成效，供未來推廣副產石灰資源化之用。研究結果得知，CFB飛灰使用於水泥-爐石粉系統中最佳用量範圍約在20%，而CFB飛灰用量超過25%時，則會造成體積過量膨脹或無法有效抑制乾縮。而在混凝土方面，副產石灰掺配爐石粉製作混凝土，會產生緩凝效應，透過調整使用藥劑，及減少拌和用水量的方式可則使凝結時間可與不添加CFB飛灰之混凝土相近，而參考強度210 kgf/cm2及280 kgf/cm2之配比，在強度方面皆能達到要求。在現地澆注部分，添加CFB飛灰之混凝土鑽心試體抗壓強度亦皆能達到參考強度之要求，現地製作試體耐久性測試結果亦優於為添加CFB飛灰之配比，顯示CFB飛灰為極具潛力之資源化副產品。 Petroleum coke combustion occurs inside the body of Circulating Fluidized Bed Boiler, referred to as CFB, in order to generate power. To avoid excess emissions of sulfur oxides from the high post-combustion sulfur content of petroleum coke, limestone is added, generating a by-products, namely, lime CFB byproduct. In this study, the development in the utilization of fly ash from lime CFB byproduct as cement is researched. The quality as cementing materials from lime CFB byproducts were evaluated for various batch. Feasibility of using lime CFB byproducts were then assessed and a database established. In addition, lime CFB cement was used for concrete application. Different mixes were produced and laboratory tests on the durability of concrete made with CFB fly ash were conducted to evaluate the long-term effectiveness of using concrete made from lime CFB byproducts and to evaluate future promotion in the utilization of resources from lime by-products. Research results show that, CFB fly ash were best used in cement when the fly ash content was about 20%. The use of CFB fly ash by amount of more than 25% will cause excessive volume expansion or uncontrolled shrinkage. In concrete, the use of lime flyash by-product would cause retardation effect during the production of concrete. By adjusting admixtures and reducing the mixing water, the setting time is extended. In comparison to concretes made with non-CFB fly ash with a reference strength intensity of 210 kgf/cm2, the strength of 280 kgf/cm2 produced is able to meet the requirement. The addition of CFB fly ash has met the requirements of compressive strength of the reference concrete. Durability test results have shown that the addition of CFB is better than that of ordinary fly ash, indicating CFB fly ash great potential use as a by-product resources for concrete production.
显示于类别:	[土木工程研究所] 博碩士論文