中大機構典藏-NCU Institutional Repository-提供博碩士論文、考古題、期刊論文、研究計畫等下載:Item 987654321/1735
English  |  正體中文  |  简体中文  |  Items with full text/Total items : 80990/80990 (100%)
Visitors : 40820598      Online Users : 1492
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version


    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/1735


    Title: 以液態電遷移製備鎂基化合物;Fabrication of Mg-based compound by Liquid Electromigration
    Authors: 李卓憲;Cho-hsien Li
    Contributors: 材料科學與工程研究所
    Keywords: 儲氫;液態電遷移;Hydrogen storage;liquid electromigration
    Date: 2007-06-22
    Issue Date: 2009-09-21 11:28:59 (UTC+8)
    Publisher: 國立中央大學圖書館
    Abstract: 本研究成功地利用液態電遷移之方式製備出Mg2Ni化合物。將電流通過鎳/熔融鎂/鎳三明治結構,在熔融鎂中之鎳原子會受電遷移之效應被推向陽極界面且在熔融鎂/鎳界面生成厚的Mg2Ni化合物,而通電流之化合物厚度遠大於無電流之情形,這暗示電流可以增加界面化合物的生長。另外,從XRD分析,繞射圖中僅有(110)繞射峰,此顯示電遷移成長出之Mg2Ni化合物為單晶或有一優選方向之結構。由此觀察而知,在陽極界面生成之Mg2Ni化合物與電流方向有密切相關性。 In this study, we have successfully produced Mg2Ni compound phase by using liquid-electromigration method. By applying a current flow through Ni/molten Mg/Ni sandwich structure, the Ni atoms in the molten Mg were electromigrated toward the anode interface and formed a thick layer of Mg2Ni compound at the anode molten Mg/Ni interface. The formation of the interfacial Mg2Ni compound is much larger than that in the no-current case. It implies that the growth of the interfacial Mg2Ni compound can be enhanced by the current-stressing. Remarkably, from XRD analysis, EM-grown Mg2Ni phase show a single crystal nature, only one single peak ((110) plane) appears in the XRD diffraction pattern. This observation suggests that the formation of EM-grown Mg2Ni compound at the anode interface highly corresponds to the direction of the electron flow.
    Appears in Collections:[Institute of Materials Science and Engineering] Electronic Thesis & Dissertation

    Files in This Item:

    File SizeFormat


    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 隱私權政策聲明