English  |  正體中文  |  简体中文  |  Items with full text/Total items : 66984/66984 (100%)
Visitors : 22949901      Online Users : 626
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version


    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/2118


    Title: Cu/Mg比與熱處理對Al-Cu-Mg-Ag合金應力腐蝕性之影響
    Authors: 莊雅傑;Ya-Chieh Chuang
    Contributors: 機械工程研究所
    Keywords: 熱處理;應力腐蝕破裂;stress corroson crack;Al-Cu-Mg-Ag
    Date: 2002-07-04
    Issue Date: 2009-09-21 11:38:46 (UTC+8)
    Publisher: 國立中央大學圖書館
    Abstract: 摘要 Al-Cu-Mg-Ag合金為一高強度鋁合金,隨著Cu/Mg比由大到小,強化機制由Ω及θ’相並重至Ω相為主要強化相,且當施行不同熱處理,晶界析出形態也跟著改變,應力腐蝕破裂是Al-Cu-Mg-Ag合金破裂的重要原因之一,其破壞性會隨著析出形態而改變,故本研究探討主題為Cu/Mg比與熱處理對Al-Cu-Mg-Ag合金應力腐蝕破裂之影響。 本研究設計不同Cu/Mg比(Cu/Mg重量比=4、8、19、29)之四種合金,施以不同的時效熱處理(T4、T6、T7、RRA),探討在應力腐蝕環境之下,各種時效熱處理條件對應力腐蝕敏感性的影響。利用光學顯微鏡(OM)、掃描式電子顯微鏡(SEM)、穿透式電子顯微鏡(TEM)、微差掃描熱分析儀(DSC)、導電度(%IACS)、硬度試驗、拉伸試驗(Tensile Test)與慢應變速率試驗(SSRT)等方法,探討微結構的變化與材料機械性質與抗應力腐蝕敏感性之關係。再根據實驗結果,尋求一兼具高強度與高抗應力腐蝕破壞Al-Cu-Mg-Ag鋁合金的製造方法及合金成份設計。 由結果可知,Cu/Mg重量比=8、19在進行T6、T7與RRA時效熱處理後均擁有高強度,但其中以Cu/Mg重量比=19實施T7時效熱處理之抗應力腐蝕最為顯著;顯示出Mg含量越多,雖然使析出相分布更為細密,卻也造成晶界處陽極溶解效應越趨嚴重;而T7熱處理,晶界析出物粗大且不連續,也使得抗應力腐蝕破裂效果較T6、RRA佳。
    Appears in Collections:[機械工程研究所] 博碩士論文

    Files in This Item:

    File SizeFormat
    0KbUnknown674View/Open


    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明