English  |  正體中文  |  简体中文  |  Items with full text/Total items : 65317/65317 (100%)
Visitors : 21323480      Online Users : 227
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version


    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/2119


    Title: Cu/Mg比對Al-Cu-Mg-Ag合金熱穩定性之影響
    Authors: 徐梓益;Tiz-Yi Hsu
    Contributors: 機械工程研究所
    Keywords: 熱穩定性;Al-Cu-Mg-Ag;thermal stability
    Date: 2002-07-09
    Issue Date: 2009-09-21 11:38:47 (UTC+8)
    Publisher: 國立中央大學圖書館
    Abstract: Al-Cu-Mg-Ag合金為一可熱處理型鋁合金,強化相Ω相及θ’相析出受Cu/Mg比影響。由於Ω相在鋁基地主要滑動面{111}α上析出,且Ω相具高溫穩定性,不僅可增加材料機械強度,亦使材料於高溫長時間下有好的熱穩定性。由於Al-Cu-Mg-Ag合金析出行為受Cu/Mg比影響,本研究探討不同Cu/Mg比對Al-Cu-Mg-Ag合金熱穩定性之影響。 實驗設計四種Cu/Mg比(Mg含量)試片,分別為29(0.16wt.% Mg)、19(0.25 wt.% Mg)、8(0.56 wt.% Mg)、4(1.12 wt.% Mg)的Al-4.6Cu-Mg-0.6Ag(wt.%)合金,經T7熱處理後置於高溫107℃、135℃、155℃持溫1000小時後,以光學顯微鏡(OM)、電子微探儀(EPMA)、導電度(%IACS)、微差掃描熱分析(DSC)、掃描式電子顯微鏡(SEM)與穿透式電子顯微鏡(TEM)分析微結構變化,機械性質測試則進行拉伸試驗與硬度試驗,透過機械性質的分析,以了解Cu/Mg比對Al-Cu-Mg-Ag合金於高溫下之微結構上的差異,如何影響合金機械性質及熱穩定性。 含1.12wt.%Mg的合金,因Mg含量過高,加工硬化現象極為明顯,造成擠型性不佳,極易於擠型時產生巨大的裂縫,故不對其進行熱穩定性研究。 由DSC及TEM分析可知,合金於T7熱處理後,隨著Mg含量的增加(Cu/Mg比降低),Ω相析出量增加且漸為主要強化相;由熱穩定性的硬度曲線可知,硬度曲線的下降幅度,隨Mg含量的增加(Cu/Mg比降低)而趨緩,由此可知,合金中Ω相愈多,於高溫長時間時效的熱穩定性愈好。
    Appears in Collections:[機械工程研究所] 博碩士論文

    Files in This Item:

    File SizeFormat
    0KbUnknown638View/Open


    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明