    题名: Electrochemical properties of LiFePO4 prepared via ball-milling
    作者: Fey,GTK;Chen,YG;Kao,HM
    贡献者: 化學工程與材料工程學系
    关键词: LITHIUM IRON PHOSPHATE;SOLID-STATE SYNTHESIS;CATHODE MATERIALS;HYDROTHERMAL SYNTHESIS;COMPOSITE CATHODES;ROOM-TEMPERATURE;BATTERY CATHODES;ION BATTERIES;PARTICLE-SIZE;PERFORMANCE
    日期: 2009
    上传时间: 2010-06-29 17:26:51 (UTC+8)
    出版者: 中央大學
    摘要: LiFePO4 cathode materials with distinct particle sizes were prepared by a planetary ball-milling method. The effects of particle size on the morphology, thermal stability and electrochemical performance of LiFePO4 cathode materials were investigated. The ball-milling method decreased particle size, thereby reducing the length of diffusion and improving the reversibility of the lithium ion intercalation/deintercalation. It is worth noting that the small particle sample prepared using malonic acid as a carbon source achieved a high capacity of 161 mAh g(-1) at a 0.1 C rate and had a very flat capacity curve during the early 50 cycles. However, the big particle samples (similar to 400 nm) decayed more dramatically in capacity than the small particle size samples (similar to 200nm) at high current densities. The improvement in electrode performance was mainly due to the fine particles. the small size distribution, and the increase in electronic conductivity as a result of carbon coating. The structure and morphology of the ground LiFePO4 samples were characterized with XRD, FE-SEM, TEM, EDS, and DSC techniques. (C) 2008 Elsevier B.V. All rights reserved.
    關聯: JOURNAL OF POWER SOURCES
    显示于类别:[化學工程與材料工程研究所] 期刊論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    index.html0KbHTML704检视/开启


    在NCUIR中所有的数据项都受到原著作权保护.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈  - 隱私權政策聲明