Hydrogenation of p-chloronitrobenzene over NiPtB nanoalloy catalysts

NCU Institutional Repository > 工學院 > 化學工程與材料工程研究所 > 期刊論文 > Item 987654321/26400

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26400

题名:	Hydrogenation of p-chloronitrobenzene over NiPtB nanoalloy catalysts
作者:	Chen,YW;Sasirekha,N;Liu,YC
贡献者:	化學工程與材料工程學系
关键词:	LIQUID-PHASE HYDROGENATION;SELECTIVE HYDROGENATION;O-CHLORONITROBENZENE;SYNTHESIS PARAMETERS;NANOMETAL CATALYSTS;COLLOIDAL CATALYSTS;AMORPHOUS CATALYSTS;NI;FE;CO
日期:	2009
上传时间:	2010-06-29 17:27:11 (UTC+8)
出版者:	中央大學
摘要:	NiPtB nanoalloy catalysts with various Ni contents were prepared by chemical reduction method at room temperature using NaBH4 as reducing agent. Pt and Ni cations were completely reduced to metals, and small amount of boron was also reduced and form alloy with metals. NiPtB formed nanosized alloy structure and X-ray diffraction patterns showed its amorphous nature. The particle size distribution and the surface composition were affected by Ni/Pt ratio in the starting materials and the temperature of heat treatment. The catalytic activity of the nanoalloys was tested for hydrogenation of p-chloronitrobenzene (p-CNB). The activity and selectivity to p-chloroaniline (p-CAN) were affected by the content of Ni in the catalyst. For NiPt0.01B catalyst, the occurrence of surface segregation of B was driven by the strain energy at high reaction temperature. For NiPt0.03B and NiPt0.01B catalysts. Pt segregated to the surface by H-2 affinity. Ni/Pt ratio decreased as the reaction temperature increased. The activity was essentially affected by the addition of Ni on Pt in the NiPtB catalyst, as expected, because Pt is more active than Ni for this reaction. The hydrogenation of p-CNB was very selective and yielded p-CAN exclusively on NiPtB catalysts than that on Pt catalyst. (C) 2009 Elsevier B.V. All rights reserved.
關聯:	JOURNAL OF NON-CRYSTALLINE SOLIDS
显示于类别:	[化學工程與材料工程研究所] 期刊論文