Preparation of Phase Change Materials Microcapsules by Using PMMA Network-Silica Hybrid Shell Via Sol-Gel Process

NCU Institutional Repository > 工學院 > 化學工程與材料工程研究所 > 期刊論文 > Item 987654321/26421

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26421

题名:	Preparation of Phase Change Materials Microcapsules by Using PMMA Network-Silica Hybrid Shell Via Sol-Gel Process
作者:	Chang,CC;Tsai,YL;Chiu,JJ;Chen,H
贡献者:	化學工程與材料工程學系
关键词:	THERMAL-ENERGY STORAGE;N-OCTADECANE;MICROENCAPSULATION;FABRICATION;HEXADECANE;STABILITY;SYSTEM;PCM
日期:	2009
上传时间:	2010-06-29 17:27:40 (UTC+8)
出版者:	中央大學
摘要:	Encapsulation of phase change materials (PCM) using a poly(methyl methacrylate) network-silica hybrid as the shell material has been developed. n-Octadecane melted at 28 degrees C was used as PCM. Based on the suspension polymerization process, the microcapsules were prepared Successfully by mixing and by the reaction of ethylene glycol dimethacrylate with precopolymer solution with tetraethoxysilane (TEOS), whose resultant microcapsules had higher latent heat (AH = 151 J/g) than those without TEOS (AH = 88.3 J/g). The average size of the PCM microcapsules was about 10 pm. The silica content, n-octadecane content, and latent heat of microcapsules were changed with varying ageing conditions, ageing time, and temperature. The highest amount of latent heat (Delta H = 178.9 J/g) and n-octadecane content (73.3%) of the microcapsule were obtained when the inorganic/organic ratio of the microcapsule was 5%. It was difficult to increase n-octadecane content (74% to 55.7-67.9%) and latent heat (180.5 J/g to 135.9-165.7 J/g) of the microcapsules by introducing different functional groups of coupling agents. 0 2009 Wile), Periodicals, Inc. J Appl Polym Sci 112: 1850-1857, 2009