Synthesis of TiO2 sol in a neutral solution using TiCl4 as a precursor and H2O2 as an oxidizing agent

NCU Institutional Repository > 工學院 > 化學工程與材料工程研究所 > 期刊論文 > Item 987654321/26443

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26443

題名:	Synthesis of TiO2 sol in a neutral solution using TiCl4 as a precursor and H2O2 as an oxidizing agent
作者:	Sasirekha,N;Rajesh,B;Chen,YW
貢獻者:	化學工程與材料工程學系
關鍵詞:	CHEMICAL-VAPOR-DEPOSITION;POROUS ANATASE TIO2;DIOXIDE THIN-FILMS;PHOTOCATALYTIC OXIDATION;OPTICAL-PROPERTIES;LOW-TEMPERATURE;GEL PREPARATION;NANOCRYSTALLINE;HYDROLYSIS;POWDERS
日期:	2009
上傳時間:	2010-06-29 17:28:10 (UTC+8)
出版者:	中央大學
摘要:	Nanosize TiO2 thin film on glass substrate was obtained through dip-coating method using TiO2 sol. Suspended nanosize TiO2 sols with anatase structure in aqueous solution were synthesized by sol-gel method using TiCl4 as a precursor. TiCl4 was reacted with an aqueous solution of NH4OH to form Ti(OH)(4), and H2O2 was then added to form peroxo titanic acid. It was further heated in water and converted to TiO2. The effects of the preparation parameters, viz., pH value of the Ti(OH)(4) gel, concentration of H2O2, and heating temperature and time, on the properties of the TiO2 sol were investigated. The materials were characterized by X-ray diffraction, Fourier transform-infrared spectroscopy, and transmission electron microscopy. The results showed that the primary TiO2 particles were rhombus with the major axis ca. 10 nm and minor axis ca. 4 nm, and were in anatase structure. The sol was excellent in dispersibility and was stable in neutral and even slight basic conditions for at least 2 years without causing agglomeration. The best preparation condition was optimized with the pH value of Ti(OH)(4) gel at 8, H2O2/TiO2 mole ratio of 2, and heating at 97 degrees C for 8 h. The transparent adherent TiO2 film on glass substrates exhibits strong hydrophilicity after illuminating with ultraviolet light and it can be used as an efficient photocatalyst. (C) 2009 Elsevier B.V. All rights reserved.