The effect of carbon coating thickness on the capacity of LiFePO4/C composite cathodes

NCU Institutional Repository > 工學院 > 化學工程與材料工程研究所 > 期刊論文 > Item 987654321/26445

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26445

题名:	The effect of carbon coating thickness on the capacity of LiFePO4/C composite cathodes
作者:	Cho,YD;Fey,GTK;Kao,HM
贡献者:	化學工程與材料工程學系
关键词:	LITHIUM-ION BATTERIES;ELECTROCHEMICAL PROPERTIES;PHOSPHO-OLIVINES;IRON PHOSPHATES;PERFORMANCE;ROUTE;TEMPERATURE;ELECTRODES;BEHAVIOR;CELLS
日期:	2009
上传时间:	2010-06-29 17:28:14 (UTC+8)
出版者:	中央大學
摘要:	Two types of carbon source and precursor mixing pellets were employed simultaneously to prepare the LiFePO4/C composite materials: Type I using the LiFePO4 precursor with 20 wt.% polystyrene (PS) as a primary carbon source, and Type II using the LiFePO4 precursor with 50 wt.% malonic acid as a secondary carbon vapor source. During final sintering, a Type I pellet was placed down-stream and Type II precursor pellet(s) was(were) placed upstream next to a Type I precursor pellet in a quartz-tube furnace. The carbon-coated product of the sintered Type I precursor pellet was obtained by using both PS and malonic acid as carbon sources. When two Type II pellets were used as a carbon vapor source (defined as Product-2), a more uniform film between 4 and 8 nm was formed, as shown in the TEM images. In the absence of a secondary carbon source (defined as Product-0), the discharge capacity of Product-0 was 137 mAh g(-1) with 100 cycles at a 0.2C-rate, but Product-2 demonstrated a high capacity of 151 mAh g(-1) with 400 cycles. Our results indicate that electrochemical properties of LiFePO4 are correlated to the amount of carbon and its coating thickness and uniformity. (C) 2008 Elsevier B.V. All rights reserved.