English  |  正體中文  |  简体中文  |  Items with full text/Total items : 69937/69937 (100%)
Visitors : 23350234      Online Users : 593
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version


    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/26451


    Title: Thermal and electrochemical behavior of yttria-stabilized zirconia coated LiCoO2 during overcharge tests
    Authors: Fey,GTK;Hsiao,CL;Muralidharan,P
    Contributors: 化學工程與材料工程學系
    Keywords: RECHARGEABLE LITHIUM BATTERIES;LI-ION CELL;CATHODE MATERIALS;ENHANCED CYCLABILITY;4.5 V;ELECTROLYTE;PERFORMANCE;IMPROVEMENT
    Date: 2009
    Issue Date: 2010-06-29 17:28:22 (UTC+8)
    Publisher: 中央大學
    Abstract: Sol-gel synthesized yttria-stabilized zirconia (YSZ) ceramic powders were coated on LiCoO2 cathode particles by a simple mechano-thermal process, calcined at 923 K for 10 h. The XRD patterns of YSZ-coated LiCoO2 revealed a single-phase hexagonal alpha-NaFeO2-type structure with Rim symmetry of the core material without any modification. The surface of LiCoO2 particles was coated with a uniform layer of YSZ that had an average thickness of similar to 20 run, as observed from TEM images. The different binding energies of O 1 s XPS data exhibited the presence of oxygen ions corresponding to the surface coated YSZ and LiCoO2. The galvanostatic cycling studies for the coated materials suggest that 2.0 wt.% YSZ-coated LiCoO2 delivered a stable capacity of 160 mAh g(-1) between 2.75 V and 4.4 V vs. Li and a good cycle stability of about 142 cycles. The impedance growth was slower for LiCoO2 surface coated with YSZ, when cells were charged at 4.4 V and 4.5 V. DSC results illustrated that the oxygen evolution exothermic peak at about 458 K was significantly smaller for YSZ-coated cathode materials. (C) 2008 Elsevier B.V. All rights reserved
    Relation: JOURNAL OF POWER SOURCES
    Appears in Collections:[化學工程與材料工程研究所] 期刊論文

    Files in This Item:

    File Description SizeFormat
    index.html0KbHTML370View/Open


    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明