Formation and absence of intermetallic compounds during solid-state reactions in the Ni-Bi system

NCU Institutional Repository > 工學院 > 化學工程與材料工程研究所 > 期刊論文 > Item 987654321/26466

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26466

題名:	Formation and absence of intermetallic compounds during solid-state reactions in the Ni-Bi system
作者:	Lee,MS;Chen,C;Kao,CR
貢獻者:	化學工程與材料工程學系
關鍵詞:	DIFFUSION;ALUMINUM
日期:	1999
上傳時間:	2010-06-29 17:28:43 (UTC+8)
出版者:	中央大學
摘要:	The reactions between Ni and NiBi3 at 330, 370, 410, and 450 degrees C were studied. The compound NiBi3 was prepared by melting a mixture of 99.9994% Bi shots and 99.996%, -120 mesh Ni powder. It was found that the synthesized NiBi3- is soft and brittle. This is contrary to the characteristics of common intermetallics, which are often hard and brittle. Such inferior mechanical properties make the formation of NiBi3 in solder joints very undesirable. The reaction product was a layer of NiBi that grew parabolically, suggesting diffusion-controlled kinetics. The activation energy for the growth of NiBi is 84 kJ/mol. The fact that NiBi formed here, but not in the reaction between Ni and Bi as reported in the literature, suggests that the reason for absence of NiBi is not due to difficulty in nucleation. The more likely reason is that the interdiffusion coefficient of NiBi is much smaller than that of NiBi3. The dominant diffusing species in NiBi was analyzed by a marker movement experiment, IL was found that the Bi flux through NiBi is 3-9 times greater than Ni flux at 370 degrees C, An expression relating the marker position to the ratio of Bi flux to Ni flux was proposed.
關聯:	CHEMISTRY OF MATERIALS
顯示於類別:	[化學工程與材料工程研究所] 期刊論文