Kevlar fiber-epoxy adhesion and its effect on composite mechanical and fracture properties by plasma and chemical treatment

NCU Institutional Repository > 工學院 > 化學工程與材料工程研究所 > 期刊論文 > Item 987654321/26607

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26607

题名:	Kevlar fiber-epoxy adhesion and its effect on composite mechanical and fracture properties by plasma and chemical treatment
作者:	Wu,SR;Sheu,GS;Shyu,SS
贡献者:	化學工程與材料工程學系
关键词:	SURFACE MODIFICATION;ARAMID FIBERS;INTERFACIAL ADHESION;MATRIX INTERFACE;CARBON-FIBERS;GAS PLASMAS;IMPROVEMENT;RESIN
日期:	1996
上传时间:	2010-06-29 17:32:14 (UTC+8)
出版者:	中央大學
摘要:	Kevlar 49 fibers were surface-modified by NH3-, O-2-, and H2O-plasma etching and chlorosulfonation and subsequent reaction with some reagents (glycine, deionized water, ethylenediamine, and l-butanol) to improve the adhesion to epoxy resin. After these treatments, the changes in fiber topography, chemical compositions of the fiber surfaces, and the surface functional groups introduced to the surface of fibers were identified by SEM, XPS, and static SIMS. Interlaminar shear strength (ILSS) and T-peel strength between the fiber and epoxy resin, as measured by the short-beam test and T-peel test, were remarkedly improved by gas plasma and chlorosulfonation (0.1% and 0.25% ClSO3H at 30 s). However, from the results of similar G(IC) values of the treated and untreated fiber composites, it is clear that the fiber/matrix interfacial bond strength is only a minor contributor to G(IC). SEM was also used to study the surface topography of the fracture surfaces of composites in T-peel test. It could be seen from SEM observations that the improvement of fiber/matrix interfacial bond strength often accompanied a change in fracture mode from the interface of fiber/epoxy resins to the fiber fibrillation and the resins. (C) 1996 John Wiley & Sons, Inc.