Fabrication of Precision Scaffolds Using Liquid-Frozen Deposition Manufacturing for Cartilage Tissue Engineering

NCU Institutional Repository > 工學院 > 機械工程研究所 > 期刊論文 > Item 987654321/26861

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26861

题名:	Fabrication of Precision Scaffolds Using Liquid-Frozen Deposition Manufacturing for Cartilage Tissue Engineering
作者:	Yen,HJ;Hsu,SH;Tseng,CS;Huang,JP;Tsai,CL
贡献者:	機械工程研究所
关键词:	ARTICULAR-CARTILAGE;II COLLAGEN;OSTEOCHONDRAL DEFECTS;MECHANICAL-PROPERTIES;CHONDROCYTES;ARCHITECTURE;BONE;ADHESION;POLYMER;REPAIR
日期:	2009
上传时间:	2010-06-29 18:01:55 (UTC+8)
出版者:	中央大學
摘要:	The fused deposition manufacturing (FDM) system has been used to fabricate tissue-engineered scaffolds with highly interconnecting and controllable pore structure, although the system is limited to a few materials. For this reason, the liquid-frozen deposition manufacturing (LFDM) system based on an improvement of the FDM process was developed. Poly(D,L-lactide-co-glycolide) (PLGA) precision scaffolds were fabricated using LFDM from PLGA solutions of different concentrations. A greater concentration of PLGA solution resulted in greater mechanical strength but also resulted in less water content and smaller pore size on the surface of the scaffolds. LFDM scaffolds in general had mechanical strength closer to that of native articular cartilage than did FDM scaffolds. Neocartilage formation was observed in LFDM scaffolds seeded with porcine articular chondrocytes after 28 days of culture. Chondrocytes in LFDM scaffolds made from low concentrations (15-20%) of PLGA solution maintained a round shape, proliferated well, and secreted abundant extracellular matrix. In contrast, the FDM PLGA scaffolds had low cell numbers and poor matrix production because of heavy swelling. The LFDM system offered a useful way to fabricate scaffolds for cartilage tissue-engineering applications.