Effect of pre-aging on precipitation hardening in Al-Si-Mg alloys

NCUIR > Engineering College > Graduate Institute of Mechanical Engineering > journal & Dissertation > Item 987654321/26959

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/26959

Title:	Effect of pre-aging on precipitation hardening in Al-Si-Mg alloys
Authors:	Lee,SL;Tan,YH;Yie,SN;Lin,JC
Contributors:	機械工程研究所
Keywords:	A357 ALLOYS
Date:	1998
Issue Date:	2010-06-29 18:04:12 (UTC+8)
Publisher:	中央大學
Abstract:	The effects of various water quenching temperatures and duration time of aging on the precipitation hardened Al-7Si-0.65Mg cast alloy are investigated by differential scanning calorimetry, electrical conductivity, hardness and measurements of tensile properties. The results show a positive response to 95 degrees C water quench from solid solution treatment. The largest hardening rate can be obtained at 95 degrees C water-quenching and 60 min natural aging time. The tensile strength and hardness following a 95 degrees C quench are found to be superior to that of a 25 degrees C and 60 degrees C water quench for the shorter artificial aging time. High temperature water-quenching parameters available to high temperature (>180 degrees C) artificial aging with the shorter time are obtained.
Relation:	SCANDINAVIAN JOURNAL OF METALLURGY