Tribological characteristics of short glass fibre reinforced polycarbonate composites

NCU Institutional Repository > 工學院 > 機械工程研究所 > 期刊論文 > Item 987654321/27015

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/27015

题名:	Tribological characteristics of short glass fibre reinforced polycarbonate composites
作者:	Ho,KC;Jeng,MC
贡献者:	機械工程研究所
关键词:	FIBER ORIENTATION;RESIDUAL-STRESSES;INJECTION;POLYMERS;BEHAVIOR
日期:	1997
上传时间:	2010-06-29 18:05:36 (UTC+8)
出版者:	中央大學
摘要:	Polymeric composite material products are manufactured by injection moulding and are valued for their good mechanical and tribological properties, Various filler reinforcements are frequently added to the base materials to improve the wear and impact properties. The present study analyses the wear behaviour of polycarbonate reinforced with 20 wt.% short glass fibres. The specimens were prepared under different moulding conditions, with varied filling time, malt temperature, and mould temperature, Friction and wear tests were performed with a Schwingum Reibung Verschleiss (SRV oscillation friction wear) ball-on-plane tester, The worn surface was examined with scanning electron microscopy. The results indicate that the wear volume loss in the sliding direction perpendicular to the melt flow direction is usually lower than that in the sliding direction parallel with the melt Bow direction, The optimum injection moulding conditions for lowest wear volume loss are a filling time of 5 s, melt temperature of 290 degrees C, and mould temperature of 80 degrees C, when the sliding direction is parallel with the melt flow direction, The effects of wear volume loss are influenced significantly by the thickness of the frozen layer and the fibre orientation with respect to the sliding direction, The higher the wear volume loss, the higher is the friction coefficient, The wear volume loss in the sliding direction parallel with the melt Bow direction is in good agreement with the distribution of the frozen layer thickness. Grooves, cracks, cutting of fibres and debonding of fibres are the major wear mechanisms found in wear tests of short glass fibre reinforced polycarbonate. (C) 1997 Elsevier Science S.A.
關聯:	WEAR
显示于类别:	[機械工程研究所] 期刊論文