DYNAMICS OF GRAPHITE-EPOXY COMPOSITE UNDER DELAMINATION FRACTURE AND ENVIRONMENTAL-EFFECTS

NCU Institutional Repository > 工學院 > 機械工程研究所 > 期刊論文 > Item 987654321/27063

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/27063

题名:	DYNAMICS OF GRAPHITE-EPOXY COMPOSITE UNDER DELAMINATION FRACTURE AND ENVIRONMENTAL-EFFECTS
作者:	LAI,JY;YOUNG,KF
贡献者:	機械工程學系
关键词:	SPECIMENS
日期:	1995
上传时间:	2010-06-29 18:06:47 (UTC+8)
出版者:	中央大學
摘要:	The purpose of this work was to investigate the dynamics of a graphite/epoxy composite material with delamination fracture under various environmental conditions. Modal testing is proposed as a nondestructive method to evaluate the effects of a delamination crack on the natural frequency and damping ratio. The effects of both thermal damage and moisture content on the graphite/ epoxy composite material were studied. The experimental impulse responses were compared with simulated values. The results show that the fundamental mode dominates the dynamic characteristics and that the delamination crack may decrease the natural frequency, but increase the damping ratio of the specimen. After the specimen was exposed to high temperatures, the stiffness and hence the natural frequency were increased. The damping ratio was decreased significantly after the specimen was subjected to prolonged exposure to a humid environment. From correlation between modal parameters and delamination cracks, it was found that the method of modal analysis was suitable for nondestructive evaluation of composite materials.
關聯:	COMPOSITE STRUCTURES
显示于类别:	[機械工程研究所] 期刊論文