    题名: Study on the turning characteristics of alumina-based ceramics
    作者: Yan,BH;Huang,FY;Chow,HM
    贡献者: 機械工程學系
    关键词: N/A
    日期: 1995
    上传时间: 2010-06-29 18:07:16 (UTC+8)
    出版者: 中央大學
    摘要: In this study, the machinability of advanced ceramics sintered at three different sintering temperatures is investigated. The results show that although pre-sintered (1300 degrees C/30 min) ceramics can be machined with both carbide tools and ceramic tools, the tools sustain significant levels of tool wear after a very short period of machining. The best overall performance is achieved by using the diamond tool; the latter also being found to be essentially the only tool which can be used to machine the fine-sintered (1500 degrees C/30 min) ceramics. In addition, it is found that when cutting ceramics with a coolant or using a sucker to suck the chip from out of tool face, results in more severe tool wear than does dry cutting. The effect is contrary to that normally expected and would appear to be largely due to the chip discharge not proceeding smoothly. However, when tool face near to the cutting edge is heated and sucked, the tool wear can be improved significantly.
    關聯: JOURNAL OF MATERIALS PROCESSING TECHNOLOGY
    显示于类别:[機械工程研究所] 期刊論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    index.html0KbHTML447检视/开启


    在NCUIR中所有的数据项都受到原著作权保护.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈  - 隱私權政策聲明