Enhanced birefingence of MgF2 thin film at 193 nm by serial bideposition

NCU Institutional Repository > 理學院 > 光電科學研究所 > 期刊論文 > Item 987654321/28077

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/28077

题名:	Enhanced birefingence of MgF2 thin film at 193 nm by serial bideposition
作者:	Liu,MC;Lee,CC;Chiang,CJ;Jaing,CC
贡献者:	光電科學研究所
关键词:	VACUUM ULTRAVIOLET;DEPOSITION;ANGLE;OXIDE
日期:	2009
上传时间:	2010-06-29 19:41:20 (UTC+8)
出版者:	中央大學
摘要:	Magnesium fluoride films were coated by serial bideposition with a varying number of sub-deposited layers. The deposition angle 70A degrees remained constant throughout the process by a single electron-beam source. One, 4, 20, and 100 sub-deposition layers were prepared. The microstructure, residual stress, absorption of water, and linear birefringence of serial bideposition of anisotropic thin film at 193 nm were investigated and discussed. Microstructures of the films were observed by scanning electron microscopy. The residual stress was measured by phase-shifting interferometer. The water absorption bands of the thin films were measured by Fourier transform infrared (FTIR) spectroscopy, and refractive indices in two different directions (S- and P-polarized) were determined from a spectrometer equipped with a polarizer. The linear birefringence would increase and the stress would decrease when the sub-deposited layers were increased. When the number of layers was 100, the difference between the refractive indices for two different polarizations was able to reach 0.082.
關聯:	OPTICAL REVIEW
显示于类别:	[光電科學研究所] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
index.html		0Kb	HTML	794	检视/开启

在NCUIR中所有的数据项都受到原著作权保护.

社群 sharing