Low temperature growth of diamond-like films by cathodic arc plasma deposition

NCU Institutional Repository > 理學院 > 光電科學研究所 > 期刊論文 > Item 987654321/28215

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/28215

題名:	Low temperature growth of diamond-like films by cathodic arc plasma deposition
作者:	Chen,PL;Tsai,MY;Kao,JS
貢獻者:	光電科學研究所
關鍵詞:	CHEMICAL-VAPOR-DEPOSITION;CARBON COATINGS;EVAPORATION;OXYGEN;TRANSPORT
日期:	1996
上傳時間:	2010-06-29 19:44:07 (UTC+8)
出版者:	中央大學
摘要:	Diamond-like films with electrical resistivity exceeding 10(8) Omega . cm are grown successfully on silicon substrates at 40 degrees C in a cathodic are plasma deposition system with a steered-are source. The substrate is placed in an atmosphere of argon/oxygen mixture and RF-bias is applied. Low density graphite serves as a cathode target and a carbon source. The magnetic field due to magnets behind the graphite target makes the are spot move, The observed speed of the steered-are spot is strongly dependent on the magnitude of the applied are current and the intensity of the radial magnetic field at the surface of the target. Addition of O-2 to the system tends to improve the quality of the diamond-like films by increasing the sp(3)-C/sp(2)-C ratio and reducing the number and size of graphite microparticles with decreased deposition rate of the films, The application of RF-bias also appears to have a similar beneficial effect on the quality of the films.
關聯:	APPLIED SURFACE SCIENCE
顯示於類別:	[光電科學研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
index.html		0Kb	HTML	494	檢視/開啟

在NCUIR中所有的資料項目都受到原著作權保護.

社群 sharing