Structure characteristics contributing to flame retardancy in diazo modified novolac resins

NCU Institutional Repository > 理學院 > 化學研究所 > 期刊論文 > Item 987654321/28338

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/28338

题名:	Structure characteristics contributing to flame retardancy in diazo modified novolac resins
作者:	Wu,HH;Chu,PR
贡献者:	中央大學
关键词:	THERMAL-CHARACTERISTICS;FUNCTIONAL NOVOLAC;PHENOLIC RESINS;EPOXY-RESINS;MECHANISMS;POLYMERS;POLYMERIZATION;DEGRADATION
日期:	2009
上传时间:	2010-06-29 19:46:26 (UTC+8)
出版者:	化學研究所
摘要:	The physical characteristics of two modified novolac resins (carbonyl phenyl azo novolac resin; CPAN and 4-(4-hydroxyphenyl azo) benzyl ester novolac resin; HPDEN) bearing nitrogen and aromatic functional groups by diazo-coupling or esterification in the branch structure of phenol novolac resin were examined. Presence of the modifiers raised the phenolic decomposition temperature (5% weight loss) from 300 degrees C (pure Phenolic) to 330 degrees C and 380 degrees C, while the char residue increased from 45% to 56% and 68%, respectively. The kinetics for thermal degradation energies (E.) also rose from 151 kJ/mol K to 254 kJ/mol K (CPAN) and 273 kJ/mol K (HPDEN). The retarded decomposition kinetics is attributed both to the increase of crosslink densities and high aromatic content in the derivative resins. On the other hand, the diazo-coupling or phenyl diazenyl ester produces non-combustible gases (N-2, CO2 and CO) during formation of aromatic char which dilute the ambient oxygen gas. Both the production of gases and the retarded kinetics due to cross-linking are definitive for the improved flame resistance. (C) 2009 Elsevier Ltd. All rights reserved.