Crystallization and melting behaviors of poly(trimethylene terephthalate)

NCU Institutional Repository > 理學院 > 化學研究所 > 期刊論文 > Item 987654321/28359

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/28359

题名:	Crystallization and melting behaviors of poly(trimethylene terephthalate)
作者:	Huang,JM;Ju,MY;Chu,PP;Chang,FC
贡献者:	中央大學
关键词:	POLY(ETHER ETHER KETONE);BLENDS
日期:	1999
上传时间:	2010-06-29 19:47:00 (UTC+8)
出版者:	化學研究所
摘要:	The crystallization and melting behaviors of poly(trimethylene terephthalate) (PTT) have been studied by differential scanning calorimetry (DSC), wide-angle X-ray diffraction (WAXD), and solid-state NMR. At certain crystallization temperatures (T-c) for a given time, the isothermally crystallized PTT exhibits two melting endotherms, which is similar to that of PBT and PBT. At higher crystallization temperature (T-c = 210 degrees C), the low-temperature endotherm is related to the melting of the original crystals, while the high-temperature endotherm is associated with the melting of crystals recrystallized during the hearing. The peak temperatures of these double-melting endotherms depend on crystallization temperature, crystallization time, and cooling rate from the melt as well as the subsequent heating rate. At a low cooling rate (0.2 degrees C/min) or a high heating rate (40 degrees C/min), these two endotherms tend to coalesce into a single endotherm, which is considered as complete melting without reorganization. WAXD results confirm that only one crystal structure exists in the PTT sample regardless of the crystallization conditions even with the appearance of double melting endotherms. The results of NMR reveal that the annealing treatment increases proton spin lattice relaxation time in the rotation frame, T-1 rho(H), of the PTT. This phenomenon suggests that the mobility of the PTT molecules decreases after the annealing process. The equilibrium melting temperature (T(m)degrees) determined by the Hoffman-Weeks plot is 248 degrees C.
關聯:	JOURNAL OF POLYMER RESEARCH-TAIWAN
显示于类别:	[化學研究所] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
index.html		0Kb	HTML	495	检视/开启

在NCUIR中所有的数据项都受到原著作权保护.

社群 sharing

数据加载中.....