English  |  正體中文  |  简体中文  |  Items with full text/Total items : 65317/65317 (100%)
Visitors : 21371579      Online Users : 213
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version


    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/2910


    Title: 潤滑劑與製程參數對Al-0.8Mg-0.5Si鋁合金擠壓鑄件的影響;Effects of lubricant and processing parameters in squeeze casting Al-0.8Mg-0.5Si aluminum alloy
    Authors: 黃永森;Yung-Sen Huang
    Contributors: 機械工程研究所
    Keywords: Al-Mg-Si鋁合金;擠壓鑄造;反應膜;微孔/介在物;Al-Mg-Si aluminum alloys;squeeze cast;reaction film;pore/particle
    Date: 2007-07-07
    Issue Date: 2009-09-21 12:00:12 (UTC+8)
    Publisher: 國立中央大學圖書館
    Abstract: 本篇研究目的在討論不同的(潤滑劑、澆鑄溫度)製程參數下,利用擠壓鑄造方式得到Al- X Mg-Y Si(X:0.82~0.88wt%;Y:0.55~0.57wt%)鋁合金鑄件,並討論鑄件中微孔/介在物數目和氧化膜對於拉伸性質與疲勞性質的影響。 在拉伸性質方面,試棒在相同應變速率下,試棒中反應膜面積率越多對試棒的拉伸強度及延伸率的影響越嚴重。 在疲勞性質方面,分析兩種高低反覆應力的破壞模式與鑄件微結構改變的關係,並將反應膜面積率、介在物顆粒與疲勞曲線結合討論鑄件中微孔/介在物和氧化膜對疲勞壽命的影響。實驗結果顯示,存在於試棒表面附近的反應膜對疲勞壽命的影響較介在物顆粒的影響效果更為顯著。 擠壓鑄造Al-(0.82~0.88)Mg-(0.56~0.57)Si合金在使用石墨粉末作為潤滑劑與Die casting水性金屬模離型劑,在擠壓壓力為60MPa,澆鑄溫度750℃和模具溫度180~200℃的製程參數下可獲得較佳的機械性質。 This study focus on the investigating of the effect of pore/particle counts and reaction films on the tensile & fatigue properties of squeeze casting. The material used in this study were Al-X Mg-Y Si(X:0.82~0.88wt%;Y:0.55~0.57wt%) alloys. The tensile test was performed at the same strain rate(0.67mm/min). The reaction film plays an important role on the ultimate tensile strength and the elongation of samples. The ultimate tensile strength and elongation were decreased with the increasing the area fraction of reaction films trapped in castings. For fatigue life cycles test, when the reaction film resides at the area near the surface of specimen readily to initiate crack, and the fatigue life cycles were greatly deteriorated. The processing parameters for higher quality squeezed Al-X Mg-Y Si alloys pouring as temperature of 750℃,mold temperature 180~200℃ and squeeze pressure 60MPa,and using water base lubricant added with Graphite powder alory with die casting hydrophilic releasing agent.
    Appears in Collections:[機械工程研究所] 博碩士論文

    Files in This Item:

    File SizeFormat
    0KbUnknown435View/Open


    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明