English  |  正體中文  |  简体中文  |  Items with full text/Total items : 66984/66984 (100%)
Visitors : 22681257      Online Users : 228
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version


    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/2957


    Title: 氧化物催化劑對亞共晶Mg-Ni合金之儲放氫特性研究;Catalytic effects of oxide on hydrogen storage characteristic of hypoeutectic Mg-Ni alloy
    Authors: 高裕欽;Yu-chin Kao
    Contributors: 機械工程研究所
    Keywords: 儲氫合金;亞共晶Mg-Ni合金;XRD;吸放氫速率;absorption/desorption rate;hydrogen storage alloy;hypoeutectic Mg-Ni alloy;XRD
    Date: 2008-06-23
    Issue Date: 2009-09-21 12:01:57 (UTC+8)
    Publisher: 國立中央大學圖書館
    Abstract: 本研究擬利用鑄造法製備亞共晶Mg-15 Ni合金,而後於球磨過程中將氧化物催化劑添加至亞共晶Mg-15Ni合金中,研究氧化物催化劑對亞共晶Mg-15Ni合金儲放氫特性之影響。 由X光繞射分析結果顯示,鑄態Mg-15Ni合金為Mg及Mg2Ni兩相所構成,經球磨後其繞射峰均有明顯寬化及弱化現象,而球磨中添加氧化物於Mg-15Ni合金中亦可觀察繞射峰均有明顯寬化及弱化的現象,此外也可發現微弱的氧化物繞射峰。在活化循環上,顯示添加氧化物不需長時間活化即有吸氫反應發生,以添加Cr2O3、Fe2O3效果較為明顯;在250、300 ℃儲放氫測試下,添加氧化物催化劑於Mg-15Ni合金中對吸放氫量及吸氫速率皆有所提升,然而在300 ℃下亦具有提高放氫速率與放氫比率之效果,但在250 ℃下的放氫速率仍有相當成效的效果,顯示於250 ℃下添加氧化劑並無法有效改善放氫速率。 This research plans to utilize casting method to prepare hypoeutectic Mg-15Ni alloy, and then adds the oxide catalysts in hypoeutectic Mg-15Ni alloy by ball milled, studies the oxide catalysts to influence on hydrogen storage characteristic of hypoeutectic Mg-15Ni alloy. As-cast Mg-15Ni alloy is formed by Mg and Mg2Ni two phase by the X-rays diffraction analysis, its diffraction peaks after the ball milled are obviously broaden and weaken , and adds oxides by ball milled can also observe diffraction peak it has to be obviously broadener and weakener than As-cast Mg-15Ni alloy , in addition can find the faint oxide diffraction peak. At activation circulation, reveals addition oxide catalyst can take place to react with hydrogen promptly without activation for a long time , and effect of Cr2O3, Fe2O3 is obviously outstanding; and during pressure-composite-isothermal test at 250,300 ℃, reveals addition the oxide catalyst enhances the absorption /desorption capacity and increases hydriding/dehydriding rate for Mg-15Ni alloy, however adding the oxide catalyst enhances desorption rate and desorption ratio at 300 ℃, but a little effect for enhancing desorption rate at 250 ℃,show that addition the oxide catalyst can not improve desorption rate effectively at 250 ℃ .
    Appears in Collections:[機械工程研究所] 博碩士論文

    Files in This Item:

    File SizeFormat
    0KbUnknown459View/Open


    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明