    题名: Optical and structural properties of Eu-diffused and doped ZnO nanowires
    作者: Pan,CJ;Chen,CW;Chen,JY;Huang,PJ;Chi,GC;Chang,CY;Ren,F;Pearton,SJ
    贡献者: 光電科學研究中心
    关键词: BEAM EPITAXY;GAN;PHOTOLUMINESCENCE;GROWTH;FILMS;TM;NANOCRYSTALS;TEMPERATURE;ER
    日期: 2009
    上传时间: 2010-06-30 15:39:26 (UTC+8)
    出版者: 中央大學
    摘要: Single crystal ZnO nanowires diffused with europium (Eu) from a solid source at 900 degrees C for 1 h or doped with Eu during growth have been characterized. The ZnO nanowires were grown by chemical vapor deposition on Si substrates employing Au as a catalyst. The diameter of the resulting nanowires was similar to 200 nm with a length of 1 mu m. Photoluminescence spectra excited by a He-Cd laser at room temperature showed the green luminescence at 515 nm in Eu-diffused nanowires. A small red shift of near-band-edge emission of ZnO nanowires was observed in the diffused wires, but sharp emission from Eu-3 ions was not present. Transmission electron microscopy shows crystalline Eu2O3 formation on the diffused nanowire surface, which forms a coaxial heterostructure system. When Eu was incorporated during the nanowire growth, the sharp D-5(0)-F-7(2) transition of the Eu3+ ion at around 615 nm was observed. (C) 2009 Elsevier B.V. All rights reserved.
    關聯: APPLIED SURFACE SCIENCE
    显示于类别:[光電科學研究中心] 期刊論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    index.html0KbHTML771检视/开启


    在NCUIR中所有的数据项都受到原著作权保护.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈  - 隱私權政策聲明