    题名: Electrical and optical changes in the near surface of reactively ion etched n-GaN
    作者: Chen,JY;Pan,CJ;Chi,GC
    贡献者: 物理研究所
    关键词: PHOTOLUMINESCENCE;HYDROGEN;MIXTURE;DAMAGE;INP
    日期: 1999
    上传时间: 2010-07-08 14:01:53 (UTC+8)
    出版者: 中央大學
    摘要: Photoluminescence (PL) and ohmic contact resistance measurements were used to characterize the n-GaN surface treated with reactive ion etching (RIE). The n-GaN him was grown on a sapphire substrate by a metal organic chemical vapor deposition process. Subsequently, the GaN film was etched with BCl3 or Ar gas prior to the PL measurement and contact metal Ti/Al deposition. In PL spectra, we observed the peak shift of the impurity-related emission (yellow luminescence (YL)) for both BCl3 and Ar etched n-GaN films. The amount of this wavelength shift increases with the RIE rf power increase and depends on the species of the etching gases. The shift of the YL peak decreased after thermal annealing at 500 degrees C for 30 s. The YL peak shift may be attributed to the RIE induced surface point defects. In the ohmic contact resistance measurements, the transmission line model technique was used. The contact resistance of the RIE etched surface is around 5.4 x 10(-4) Omega cm(2). However, a lower contact resistance of 5.7 x 10(-6) Omega cm(2) was obtained for a native surface of n-GaN film. No obvious distinction between the roughness of etched and native GaN surfaces was observed by the atomic force microscope measurements. In an Xray grazing diffraction measurement, the crystalline lattice orientation and the coherent length of native n-GaN layer were better than the etched n-GaN according to the results of the rocking curve and Theta-2 Theta scan. (C) 1999 Elsevier Science Ltd. All rights reserved.
    關聯: SOLID-STATE ELECTRONICS
    显示于类别:[物理研究所] 期刊論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    index.html0KbHTML298检视/开启


    在NCUIR中所有的数据项都受到原著作权保护.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈  - 隱私權政策聲明