Magnetic order and spin reorientation in Nd0.45Ca0.55MnO3

NCU Institutional Repository > 理學院 > 物理研究所 > 期刊論文 > Item 987654321/39023

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/39023

題名:	Magnetic order and spin reorientation in Nd0.45Ca0.55MnO3
作者:	Li,WH;Wu,SY;Lee,KC;Lynn,JW;Liu,RS;Wu,JB;Huang,CY
貢獻者:	物理研究所
關鍵詞:	NEUTRON-DIFFRACTION;DOUBLE EXCHANGE;MAGNETORESISTANCE;FIELD
日期:	1999
上傳時間:	2010-07-08 14:02:29 (UTC+8)
出版者:	中央大學
摘要:	Neutron diffraction and ac magnetic susceptibility measurements have been performed to study the magnetic ordering of the Mn spins in polycrystalline Nd0.45Ca0.55MnO3. Three peaks around 260, 90, and 40 K were observed in the temperature dependence of the ac susceptibility. Structural analysis using high-resolution neutron diffraction patterns shows that the peak at 260 K is associated with the charge ordering of the Mn ions. Neutron magnetic diffraction shows that the peak at 90 K originates from the ordering of the Mn spins. Both ferromagnetic and antiferromagnetic couplings between the Mn spins were found. The spin structure in the basal plane consists of tilted ferromagnetic chains (along the [110] direction) aligned antiferromagnetically, whereas the interlayer coupling is ferromagnetic. A spin reorientation occurs below 15 K, which results in a change in the title angle. The Mn spins order at T-N approximate to 120 K, and the moment saturated at 30 K at [mu(Z)]=2.29(4)mu(B). (C) 1999 American Institute of Physics. [S0021-8979(99)26008-2].
關聯:	JOURNAL OF APPLIED PHYSICS
顯示於類別:	[物理研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
index.html		0Kb	HTML	441	檢視/開啟

在NCUIR中所有的資料項目都受到原著作權保護.

社群 sharing