    题名: Magnetic ordering in double-chain PrBa2Cu4O8
    作者: Li,WH;Wu,SY;Lin,YC;Lee,KC;Lynn,JW;Weng,SS;Hong,IP;Lin,JY;Yang,HD
    贡献者: 物理研究所
    关键词: HIGH-TEMPERATURE SUPERCONDUCTORS;NORMAL-STATE PROPERTIES;RARE-EARTH IONS;OXYGEN-PRESSURE;YBA2CU4O8;TRANSPORT;PRBA2CU3O6+X;RESISTIVITY;COMPOUND;PHASE
    日期: 1999
    上传时间: 2010-07-08 14:02:30 (UTC+8)
    出版者: 中央大學
    摘要: We have successfully synthesized a single-phase sample of double-chain PrBa2Cu4O8 at ambient oxygen pressure by employing the nitric pyrolysis method. Electrical resistivity, ac magnetic susceptibility, and neutron-diffraction measurements were performed to study the basic magnetic properties of the system. The system displayed metallic conduction, and no superconductivity was observed for temperatures down to 4.2 K. An anomaly was evident in the temperature dependence of the ac susceptibility around 200 K, where a shoulder in the resistivity was also clearly seen. The Pr spins were found to order at 17 K, with a magnetic structure that may be characterized by {1/2 1/2 l} wave vectors with l = whole integers and half integers, showing that the couplings between the Pr spins are antiferromagnetic in nature. Another transition of unknown origin is also evident around 2 K. [S0163-1829(99)03729-7].
    關聯: PHYSICAL REVIEW B
    显示于类别:[物理研究所] 期刊論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    index.html0KbHTML354检视/开启


    在NCUIR中所有的数据项都受到原著作权保护.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈  - 隱私權政策聲明