題名:	Crystal structure and magnetic ordering of Pr in (Pb0.5Cu0.5)(2)(Ba0.5Sr0.5)(2)PrCu2O8
作者:	Lin,YC;Chuang,WY;Li,WH;Lee,KC;Lynn,JW;Yang,CL;Ku,HC
貢獻者:	物理研究所
日期:	1997
上傳時間:	2010-07-08 14:05:33 (UTC+8)
出版者:	中央大學
摘要:	The crystal structure of polycrystalline PbBaSrPrCu3O8 was studied using high resolution neutron diffraction. Rietveld refinement of the diffraction pattern shows that the compound crystallizes into the Tl2Ba2YCu2O8 2212-type structure. The Pb and Cu atoms in the two (Pb,Cu)O layers are randomly mixed to form two (Pb0.5Cu0.5)O layers, and the Pa and Sr atoms are also randomly mixed to form two (Ba0.5Sr0.5)O layers, resulting in (Pb0.5Cu0.5)(2)(Ba0.5Sr0.5)(2)PrCu2O8. The magnetic ordering of the Pr ions was also studied using magnetic neutron diffraction and ac susceptibility measurements. At low temperatures, magnetic peaks presumably originating from the Pr spin ordering were observed at the {1/2 1/2 1/2 1/2}, {1/2 1/2 3/2}, and {1/2 1/2 5/2} positions. The Pr spins order at T-N approximate to 9 K with the moment direction along the c axis and the nearest-neighbor spins coupled antiferromagnetically. A cusp associated with the antiferromagnetic ordering at T-N is also clearly observed in ac susceptibility measurements. (C) 1997 American Institute of Physics.
關聯:	JOURNAL OF APPLIED PHYSICS
顯示於類別:	[物理研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
index.html		0Kb	HTML	503	檢視/開啟

在NCUIR中所有的資料項目都受到原著作權保護.

社群 sharing