CuO/Ce1-xZrxO2/Al2O3觸媒於富氫中CO的選擇性氧化反應研究; Selective oxidation of CO in excess hydrogen over CuO/Ce1-xZrxO2/Al2O3 catalysts

NCU Institutional Repository > 工學院 > 化學工程與材料工程研究所 > 博碩士論文 > Item 987654321/3936

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/3936

題名:	CuO/Ce1-xZrxO2/Al2O3觸媒於富氫中CO的選擇性氧化反應研究;Selective oxidation of CO in excess hydrogen over CuO/Ce1-xZrxO2/Al2O3 catalysts
作者:	張煒謙;Woei-Chian Chang
貢獻者:	化學工程與材料工程研究所
關鍵詞:	氧化鈰;選擇性CO氧化反應;氧化銅;CuO catalyst;selective CO oxidation;CeO2 oxide
日期:	2006-06-08
上傳時間:	2009-09-21 12:26:26 (UTC+8)
出版者:	國立中央大學圖書館
摘要:	本研究將Al2O3懸浮於Ce4+、Zr4+前驅鹽溶液中，利用共沈澱法製備Ce1-xZrxO2/Al2O3擔體，採臨濕含浸法製備CuO/Ce1-xZrxO2/Al2O3觸媒，探討觸媒於富氫中CO選擇性氧化反應特性。 XRD、TPR證實，適量的ZrO2可固溶入CeO2/Al2O3，增強Ce1-xZrxO2/Al2O3的redox特性；引入Al2O3可增加Ce1-xZrxO2共氧化物的分散性，而不影響其結構及redox特性。脈衝式CO吸附實驗與XPS證實，於CuO/Ce1-xZrxO2/Al2O3中引入少量ZrO2可促使觸媒產生更多的活性中心Cu+；而引入Al2O3則會影響Ce0.9Zr0.1O2誘發Cu+產生。少量ZrO2的引入，可增強擔體的redox特性，有助於CuO/Ce1-xZrxO2/Al2O3觸媒於CO選擇性氧化反應之活性；引入Al2O3可增加Ce1-xZrxO2利用度，但不利於反應，引入量不宜過多。CuO之負載量以7%為最佳。以7%CuO/Ce0.9Zr0.1O2/Al2O3(20%)為觸媒，轉化率達100%的溫度為95~100℃(F/W=10,000 mlhr-1g-1)，較7%CuO/ CeO2/Al2O3觸媒之105~110℃降低10℃。7%CuO/Ce0.9Zr0.1O2/Al2O3於100℃左右，都可維持近100%的選擇率，是一具有高活性與高選擇率的觸媒。CO2及H2O雖會降低7%CuO/Ce0.9Zr0.1O2/ Al2O3觸媒活性，使之達100%轉化率溫度升高至155~160℃，但觸媒仍能維持90%左右的選擇性及不錯的穩定性。7%CuO/Ce0.9Zr0.1O2/Al2O3(20%)觸媒對反應氣體具有高處理容量，提高質流比(F/W)2~3倍仍可維持高選擇率。 Preferential CO oxidation in hydrogen (PROX) is one of the key-techniques in developing low temperature polymer electrolyte membrane fuel cells (H2-PEMFC). Numerous Au-based and Pt-based catalysts have been studied on the selective oxidation of CO. But none of these noble catalysts can prevent significant losses of hydrogen by oxidation. In previous work, we have found that an appropriate amount of ZrO2 introduced into cerium oxide not only promoted the redox property of the resulted mixed-oxide Ce0.9Zr0.1O2 but also enhanced the selective oxidation of CO on CuO/Ce0.9Zr0.1O2. The best catalyst of 7%CuO/Ce0.9Zr0.1O2 is a promising candidate for replacing noble catalysts used in a PROX unit of H2-PEMFC system for removing CO. But the mixed oxide Ce0.9Zr0.1O2 from co-precipitation has a surface area only about 70 m2/g, and does not have good mechanical strength and forming properties. This work will use Al2O3 as a support for mixed oxide of Ce0.9Zr0.1O2 to improve its dispersion, mechanical strength and the easiness of forming. A new supported oxide of [Ce0.9Zr0.1O2/Al2O3] will be prepared using the co-precipitation-deposition method, its redox property and the selective oxidation of CO on CuO/[Ce0.9Zr0.1O2/Al2O3] catalyst will be examined.