具苯環、硫醚及羧酸官能基之中孔洞材料的合成與鑑定; Synthesis and Characterization of Mesoporous Silicas with Benzene, Thioether and Carboxylic Acid Functionalities

NCU Institutional Repository > 理學院 > 化學研究所 > 博碩士論文 > Item 987654321/43731

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/43731

題名:	具苯環、硫醚及羧酸官能基之中孔洞材料的合成與鑑定;Synthesis and Characterization of Mesoporous Silicas with Benzene, Thioether and Carboxylic Acid Functionalities
作者:	陳慶庭;Ching-Ting Chen
貢獻者:	化學研究所
關鍵詞:	氮氣吸脫附;中孔洞;汞;BET;SBA-1;mesoporous
日期:	2010-07-23
上傳時間:	2010-12-08 14:17:28 (UTC+8)
出版者:	國立中央大學
摘要:	本篇研究主要分為三個部分，第一部分是以 Tetraethyl orthosilicate (TEOS) 與 1,4-bis (triethoxysilyl) propane tetrasufide (BTESPTS) 為共同矽源，使用 Cetyltriethylammonium bromide (CTEABr) 為界面活性劑在溫度為 0 °C 的酸性條件下以直接合成法合成具硫醚官能基之中孔洞材料 SBA-1，並利用溶劑萃取法移除界面活性劑。藉由一系列儀器鑑定後可發現隨著 BTESPTS 的植入量增加材料的表面積、孔洞體積以及孔洞直徑都會隨之下降，最終 BTESPTS 的含量可達到 33 %，此時仍能維持中孔洞材料 SBA-1 的結構特性。在第二部份是將 TEOS 改變為 1,4-bis (trithoxysilyl)-benzene (BTEB)，以 BTEB 與 BTESPTS為共同矽源透過直接合成法合成同時具有硫醚及苯環之雙官能基中孔洞 SBA-1 材料，並改變 BTEB 與 BTESPTS 的比例關係，逐漸提高 BTESPTS 的含量藉此觀察 BTEB 與 BTESPTS 對中孔洞材料的影響。藉由一系列的儀器鑑定來觀察樣品的物化性，最後矽源莫耳比到 BTEB : BTESPTS＝2 : 1時仍能保持中孔洞材料 SBA-1 的結構特性。第三部分中是以 TEOS 與 carboxyethylsilanetriol sodium salt (CES) 為共同矽源透過直接合成法合成具有羧酸官能基的中孔洞 SBA-1 材料，期望可以合成出具有高比例羧酸官能基且穩定性佳的產物，透過各種儀器鑑定其孔洞特性。藉由一系列的儀器鑑定來觀察樣品的物化性，最後矽源莫耳比到 TEOS : CES＝2 : 1時仍能保持中孔洞材料 SBA-1 的結構特性，並藉由酸鹼滴定實驗得知其酸當量為 1.455 mmol/g。 The thesis is divided into three parts. In part one, well-ordered mesoporous silicas SBA-1 functionalized with thioether groups have been synthesized via co-condensation of Tetraethyl orthosilicate (TEOS) and 1,4-bis (triethoxysilyl) propane tetrasufide (BTESPTS) under acidic conditions. The thioether-containing units are incorporated quantitatively and reach a maximum BTESPTS loading up to 33 mol% without a significant degradation of the structural ordering of the Pm3n mesophase. In part two, well-ordered cubic mesoporous silicas SBA-1 functionalized with benzene and thioether functional groups have been successfully synthesized via the co-condensation of 1,4-bis (trithoxysilyl)-benzene (BTEB) , and BTESPTS templated by CTEABr under acidic conditions. The thioether-containing units are incorporated quantitatively and reach a maximum BTESPTS loading up to 33 mol% without a significant degradation of the structural ordering of the Pm3n mesophase. In part three, well-ordered cubic mesoporous silicas SBA-1 functionalized with carboxylic acid functional groups have been successfully synthesized via the co-condensation of TEOS , and CES templated by CTEABr under acidic conditions. The carboxylic acid functional groups-containing units are incorporated quantitatively and reach a maximum CES loading up to 33 mol% without a significant degradation of the structural ordering of the Pm3n mesophase. The materials obtained were characterized by a variety of techniques including powder X-ray diffraction (XRD), nitrogen sorption measurements , 13C and 29Si magic angle spinning (MAS), IR, scanning electron microscope (SEM) and thermogravimetric analysis (TGA).