Tris(8-hydroxyquinoline)aluminum (III) (Alq3) nanowires templated from an eggshell membrane

NCUIR > Engineering College > Department of Chemical and Materials Engineering > journal & Dissertation > Item 987654321/49911

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/49911

Title:	Tris(8-hydroxyquinoline)aluminum (III) (Alq3) nanowires templated from an eggshell membrane
Authors:	Lee,T;Chang,SC;Peng,JF
Contributors:	化學工程與材料工程學系
Keywords:	LIGHT-EMITTING DEVICES;SUBLIMATION POINT DEPRESSION;CHEMICAL-COMPOSITION;SHELL MEMBRANES;RECENT PROGRESS;THIN-FILMS;SURFACE;CRYSTALLIZATION;NANOPARTICLES;LUMINESCENCE
Date:	2010
Issue Date:	2012-03-27 16:26:16 (UTC+8)
Publisher:	國立中央大學
Abstract:	One to 2-mu m long, <= 400-nm wide amorphous tris(8-hydroxyquinoline)aluminum (III) (Alq3) nanowires (NWs) grown from the 15-min boiled outer shell membrane (OSM) of the hen's egg and from the OSM solution cast film via thermal evaporation with a source temperature of 260 degrees C and a substrate temperature of 138 degrees C under 6.7 x 10(-2) Pa gave about 1.4 to 1.7 times more photoluminescence emission than the control Alq3 sample did, which was grown from the plain glass surface. The characteristic bonding energies of C 1s X-ray photoelectron signal at 282 eV, O is signal at 529 eV and N is signal at 397 eV suggested that the relatively high NW density for the 15-min boiled OSM and the OSM solution cast film, was mainly caused by the formation of the O C-O-C O anhydride moiety and the C N group in the proteinaceous OSM at high temperature of 90 degrees C to 100 degrees C. Therefore, we proposed that the 15-min boiled OSM and the OSM solution cast film apparently served as good templates by providing nano-regions of high concentration of the O C-O-C O anhydride groups and the C N groups for nesting the Alq3 gas molecules to form nano-conical Alq3 nuclei for the growth of long and narrow NWs. (C) 2010 Elsevier B.V. All rights reserved.
Relation:	THIN SOLID FILMS
Appears in Collections:	[Department of Chemical and Materials Engineering] journal & Dissertation

Files in This Item:

File	Description	Size	Format
index.html		0Kb	HTML	421	View/Open

社群 sharing

Loading...