    題名: Effects of lanthanum-based perovskite coatings on the formation of oxide scale for ferritic SOFC interconnect
    作者: Shong,WJ;Liu,CK;Chen,CY;Peng,CC;Tu,HJ;Fey,GTK;Lee,RY;Kao,HM
    貢獻者: 化學工程與材料工程學系
    關鍵詞: FUEL-CELLS;METALLIC INTERCONNECTS;CHROMIUM VAPORIZATION;OPERATING-CONDITIONS;STEEL;ALLOY;CONDUCTIVITY
    日期: 2011
    上傳時間: 2012-03-27 16:26:52 (UTC+8)
    出版者: 國立中央大學
    摘要: Three lanthanum-based perovskite ceramic compounds, La(0.8)Ca(0.2)CrO(3), La(0.8)Sr(0.2)CrO(3), and La(0.8)Sr(0.2)MnO(3), were coated on ferritic stainless steel by the spin coating technique, and the effects on the formation of oxide scale have been investigated. The coated samples were aged at 800 degrees C in ambient air atmosphere for up to 1600h. After each ageing period, the measurement of electrical area-specific resistance (ASR) was conducted. The evolution of crystalline phases and microstructures of aged samples were examined using the X-ray diffractometer and the scanning electron microscope. It was found that the perovskite pastes could facilitate the growth of (Mn, Cr)(3)O(4) spinel phases with coarser crystalline structures and higher levels of Mn content. After 1600-h ageing, coated samples exhibited an average ASR result of similar to 3 m Omega cm(-2), approximately one-third that of the uncoated sample. The ASR difference was attributed to the Mn content and crystallite size of the spinel phase. (C) 2011 Elsevier B.V. All rights reserved.
    關聯: MATERIALS CHEMISTRY AND PHYSICS
    顯示於類別:[化學工程與材料工程學系 ] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML524檢視/開啟


    在NCUIR中所有的資料項目都受到原著作權保護.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 隱私權政策聲明