Enhanced formation of periodic arrays of low-resistivity NiSi nanocontacts on (001)Si(0.7)Ge(0.3) by nanosphere lithography with a thin interposing Si layer

NCU Institutional Repository > 工學院 > 化學工程與材料工程學系 > 期刊論文 > Item 987654321/49938

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/49938

题名:	Enhanced formation of periodic arrays of low-resistivity NiSi nanocontacts on (001)Si(0.7)Ge(0.3) by nanosphere lithography with a thin interposing Si layer
作者:	Cheng,SL;Zhan,CY;Lee,SW;Chen,H
贡献者:	化學工程與材料工程學系
关键词:	EPITAXIAL-GROWTH;MORPHOLOGICAL INSTABILITY;OPTICAL-PROPERTIES;SILICIDES;NANOPARTICLES;TEMPERATURE;NISI1-UGEU;SI1-XGEX;SILICON;(001)SI
日期:	2011
上传时间:	2012-03-27 16:26:59 (UTC+8)
出版者:	國立中央大學
摘要:	In this study, we demonstrated significant enhancement of the formation of low-resistivity NiSi nanocontacts with controlled size on (0 0 1)Si(0.7)Ge(0.3) substrates by combining the nanosphere lithography with the use of a new Ni/a-Si bilayer nanodot structure. Low-resistivity NiSi with an average size of 78 nm was observed to be the only silicide phase formed in samples annealed at 350-800 degrees C. The presence of the interposing Si layer with appropriate thickness was found to effectively prevent Ge segregation and maintain the interface stability in forming NiSi nanocontacts on (0 0 1)Si(0.7)Ge(0.3). As the annealing temperature was increased to 900 degrees C, amorphous SiO(x) nanowires were observed to grow from silicide nanocontact regions. The NSL technique in conjunction with a sacrificial Si interlayer process promises to be applicable in fabricating periodic arrays of other low-resistivity silicide nanocontacts on Si(1-x)Ge(x) substrates without complex lithography. (C) 2011 Elsevier B.V. All rights reserved.