    題名: Epitaxial growth of uniform NiSi(2) layers with atomically flat silicide/Si interface by solid-phase reaction in Ni-P/Si(100) systems
    作者: Hsu,HF;Chan,HY;Chen,TH;Wu,HY;Cheng,SL;Wu,FB
    貢獻者: 化學工程與材料工程學系
    關鍵詞: NI SILICIDE;FILMS;INTERLAYER
    日期: 2011
    上傳時間: 2012-03-27 16:27:00 (UTC+8)
    出版者: 國立中央大學
    摘要: As metal-oxide-semiconductor field-effect transistor (MOSFET) devices are shrunk to the nanometer scale, flat shallow metal/Si electrical contacts must be formed in the source/drain region. This work demonstrates a method for the formation of epitaxial NiSi(2) layers by a solid-phase reaction in Ni-P(8 nm)/Si(1 0 0) samples. The results show that the sheet resistance remained low when the samples were annealed at temperatures from 400 to 700 degrees C. P atoms can be regarded as diffusion barriers against the supply of Ni to the Si substrate, which caused the formation of Si-rich silicide (NiSi(2)) at low temperature. Furthermore, elemental P formed a stable capping layer with O, Ni and Si during the annealing process. A uniform NiSi(2) layer with an atomically flat interface was formed by annealing at 700 degrees C because of the formation of a Si-Ni-P-O capping layer and a reduction in the total interface area. (C) 2011 Elsevier B.V. All rights reserved.
    關聯: APPLIED SURFACE SCIENCE
    顯示於類別:[化學工程與材料工程學系 ] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML391檢視/開啟


    在NCUIR中所有的資料項目都受到原著作權保護.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋  - 隱私權政策聲明