Mechanical properties and thermal stability of a Cu-based bulk metallic glass microalloyed with silicon

NCU Institutional Repository > 工學院 > 化學工程與材料工程學系 > 期刊論文 > Item 987654321/49956

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/49956

題名:	Mechanical properties and thermal stability of a Cu-based bulk metallic glass microalloyed with silicon
作者:	Tsai,PH;Lee,IS;Jian,SR;Jang,JSC
貢獻者:	化學工程與材料工程學系
關鍵詞:	SUPERCOOLED LIQUID REGION;MINOR ALLOYING ADDITIONS;AMORPHOUS-ALLOYS;FORMING ABILITY;HIGH-STRENGTH;ZR-TI;NI;CRYSTALLIZATION;CO;SYSTEM
日期:	2011
上傳時間:	2012-03-27 16:27:21 (UTC+8)
出版者:	國立中央大學
摘要:	(Cu(42)Zr(42)Al(8)Ag(8))(100-x)Si(x) (x=0 similar to 1) amorphous alloy rods of 2-6 mm diameter were prepared by Cu-mold drop casting. The thermal properties, microstructure evolution, and mechanical properties were studied by differential scanning calorimetry (DSC), X-ray diffractometry (XRD), transmission electron microscopy (TEM), hardness test, and compression test. The XRD result revealed that all as-quenched (Cu(42)Zr(42)Al(8)Ag(8))(100-x)Si(x) alloy rods exhibited a broad diffraction pattern in the amorphous phase. The (Cu(42)Zr(42)Al(8)Ag(8))(99.5)Si(0.5) alloy was found to possess the highest glass forming ability (GFA) as well as the best thermal stability among all tested samples. In addition, both its hardness and yield strength were increased by the microalloyed Si content. The fracture strength and the plastic strain of (Cu(42)Zr(42)Al(8)Ag(8))(99.5)Si(0.5) amorphous alloy can reach 2000 MPa and 3.5 %.