Heat-treatment induced material property variations of Al-coated Mg alloy prepared in aluminum chloride/1-ethyl-3-methylimidazolium chloride ionic liquid

NCU Institutional Repository > 工學院 > 材料科學與工程研究所 > 期刊論文 > Item 987654321/49994

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/49994

题名:	Heat-treatment induced material property variations of Al-coated Mg alloy prepared in aluminum chloride/1-ethyl-3-methylimidazolium chloride ionic liquid
作者:	Chuang,MH;Chang,JK;Tsai,PJ;Tsai,WT;Deng,MJ;Sun,IW
贡献者:	材料科學與工程研究所
关键词:	AZ91D MAGNESIUM ALLOY;CORROSION BEHAVIOR;MOLTEN-SALT;ELECTRODEPOSITION;TRANSITION;COATINGS;AIR
日期:	2010
上传时间:	2012-03-27 16:28:25 (UTC+8)
出版者:	國立中央大學
摘要:	An Al coating film, electrodeposited on a Mg alloy from aluminum chloride-1 -ethyl-3-methylimidazolium chloride (AlCl(3)-EMIC) ionic liquid, effectively prevents the substrate from rapid corrosion in a hostile environment. The thickness of the Al film can be easily determined by controlling the total cathodic charge applied, because the current efficiency of the electrodeposition reaction is close to 100%. Heat treatment at 450 degrees C under an argon atmosphere for 10 min causes an inter-diffusion at the Al/Mg interface, optimizing the protective performance of the coating film. Prolonging heating leads to a Mg(17)Al(12) intermetallic phase and a Mg solid solution phase to be formed at the expense of the deposited Al film. This phase transformation gives rise to a degradation in the corrosion resistance of the Al-coated sample. (C) 2010 Elsevier B.V. All rights reserved.
關聯:	SURFACE & COATINGS TECHNOLOGY