    題名: Thermal and mechanical characterizations of a Zr-based bulk metallic glass composite toughened by in-situ precipitated Ta-rich particles
    作者: Jang,JSC;Jian,SR;Pan,DJ;Wu,YH;Huang,JC;Nieh,TG
    貢獻者: 材料科學與工程研究所
    關鍵詞: AMORPHOUS-ALLOYS;PLASTICITY;BEHAVIOR
    日期: 2010
    上傳時間: 2012-03-27 16:28:41 (UTC+8)
    出版者: 國立中央大學
    摘要: The Zr(53)Cu(30-x)Ni(9)Al(8)Ta(x) (x = 2, 4, 6, 8) bulk metallic glass composites (BMGCs) rods with a diameter of 2-4 mm have been successfully fabricated by suction casting method in this study. The thermal and the mechanical properties of these Zr-based BMGCs were systematically investigated by the combination of DSC, XRD, SEM, TEM, and compression test. The results show that a superior mechanical performance with up to 30% compressive plastic strain, 1750 MPa yield strength and 2100 MPa fracture strength at room temperature can be obtained for the 2 mm diameter rod of the Zr(53)Cu(22)Ni(9)Al(8)Ta(8) BMGC. There are two kinds of in-situ dispersed Ta-rich particles, micro-sized (10-30 mu m), and nano-sized (20-80 nm) were found homogeneously distributed in the amorphous matrix. These Ta-rich particles act as discrete obstacles in the amorphous matrix, which separates and restricts the highly localized shear-banding, avoiding shear-through of the whole sample. This results in the formation of multiple shear bands around the Ta-rich particles and decreases the stress concentration for further propagation of shear band, and so as to enhance plasticity dramatically. In addition, the Ta-added BMG also exhibits similar GFA in comparison with the base BMG. (C) 2009 Elsevier Ltd. All rights reserved.
    關聯: INTERMETALLICS
    顯示於類別:[材料科學與工程研究所 ] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML536檢視/開啟


    在NCUIR中所有的資料項目都受到原著作權保護.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 隱私權政策聲明