English  |  正體中文  |  简体中文  |  Items with full text/Total items : 68069/68069 (100%)
Visitors : 23168823      Online Users : 202
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version

    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/50005

    Title: Thermoplastic forming ability of a Mg-base bulk metallic glass composites reinforced with porous Mo particles
    Authors: Jang,JSC;Li,WJ;Li,TH;Jian,SR;Huang,JC;Nieh,TG
    Contributors: 材料科學與工程研究所
    Date: 2010
    Issue Date: 2012-03-27 16:28:43 (UTC+8)
    Publisher: 國立中央大學
    Abstract: The thermoplastic deformation behavior of the Mg(58)Cu(28.5)Gd(11)Ag(2.5) metallic glass composites (BMGCs) reinforced with porous Mo particles was studied by means of thermal scanning calorimetry (DSC), thermal mechanical analysis (TMA) and high-temperature compression test in the supercooled liquid region. Based on the result obtained from DSC and TMA, the deformation behavior for Mg(58)Cu(28.5) Gd(11)Ag(2.5) BMGC rod was investigated by compression test at different strain rates (1 x 10(-2)-1 x 10(-1) s(-1)) and temperatures in the supercooled liquid region, namely 433 K, 438 K. and 443 K. The flow stresses obtained at a constant strain rate of 1 x 10(-2) s(-1) decrease with increasing temperature and reach a low stress about 10 MPa at 443 K. In addition, the X-ray diffraction results confirm that the Mg(58)Cu(28.5) Gd(11)Ag(2.5) BMGC samples remain the amorphous nature after compression at 443 K. The current results indicate that the Mg(58)Cu(28.5)Gd(11)Ag(2.5) BMGC possesses an excellent superplastic formability with the m-value (strain rate sensitivity) greater than 0.7 in the supercooled liquid region of 438-443 K at a strain rate around 1 x 10(-2) s(-1). (C) 2010 Published by Elsevier Ltd.
    Appears in Collections:[材料科學與工程研究所 ] 期刊論文

    Files in This Item:

    File Description SizeFormat

    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明