    题名: Influence of Mg(3)AlNi(2) content on the cycling stability of Mg(2)Ni-Mg(3)AlNi(2) hydrogen storage alloy electrodes
    作者: Lee,SL;Hsu,FK;Chen,WC;Lin,CK;Lin,JC
    贡献者: 材料科學與工程研究所
    关键词: ELECTROCHEMICAL CHARACTERISTICS;PARTIAL SUBSTITUTION;MGNI ALLOY;NI;FE;CO
    日期: 2011
    上传时间: 2012-03-27 16:29:13 (UTC+8)
    出版者: 國立中央大學
    摘要: A novel method to improve the cycling capacity degradation of Mg(2)Ni-based hydrogen storage alloy by means of composite materials has been proposed. The new composites Mg(2)Ni-x mol% Mg(3)AlNi(2) (x = 0, 15, 30, 60, 100) were prepared by means of combining electric resistance melting with isothermal evaporation casting process (IECP). Phase analysis and microstructure were investigated by SEM and TEM observations. Results showed that the cycling stability of the alloy with Mg(3)AlNi(2) was superior to that of Mg(2)Ni. XPS analysis revealed that the formation of an Al oxide film during cycling could enhance the anti-corrosion of the surface of the composites. Among the obtained capacity retaining rates, Mg(2)Ni-15 mol% Mg(3)AlNi(2) composite had the best anti-corrosion performance. This composite has kept 76% of its maximum discharge capacity (50 mA hg(-1)) at 25th cycle compared to 20% for Mg(2)Ni. The enhancement of the cycling stability of the electrode alloy with 15 mol% Mg(3)AlNi(2) can be ascribed to the decrease in the rate of pulverization of the alloy during cycling, which is considered as the factor in the improvement of the electrochemical properties of the Mg(3)AlNi(2)-containing alloys. (C) 2011 Elsevier Ltd. All rights reserved.
    關聯: INTERMETALLICS
    显示于类别:[材料科學與工程研究所 ] 期刊論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    index.html0KbHTML695检视/开启


    在NCUIR中所有的数据项都受到原著作权保护.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 隱私權政策聲明