Preparation of Highly Adhesive and Superhydrophobic Epoxy-Based Thin Film by Sol-Gel Process

NCU Institutional Repository > 工學院 > 材料科學與工程研究所 > 期刊論文 > Item 987654321/50022

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/50022

题名:	Preparation of Highly Adhesive and Superhydrophobic Epoxy-Based Thin Film by Sol-Gel Process
作者:	Wu,GY;Wang,SS;Wu,JC;Hsu,MY;Chen,H
贡献者:	材料科學與工程研究所
关键词:	SUPER-HYDROPHOBIC FILMS;SILICA-BASED SURFACES;WATER-REPELLENT;FABRICATION;TETRAETHOXYSILANE;POLYPROPYLENE;PRECURSORS;GLYCOL
日期:	2011
上传时间:	2012-03-27 16:29:14 (UTC+8)
出版者:	國立中央大學
摘要:	In this study the preparation of a superhydrophobic epoxy-based thin film with excellent high adhesion properties was carried out by mixing epoxy polymer solution, MTMOS solution, and silica powder. It was found that the adhesion between the film and a substrate could be improved by adding PET fibers to the above solution. The characteristic properties of the as-prepared films were analyzed by contact angle measurements, scanning electron microscopy (SEM) and by atomic force microscopy (AFM). The adhesion between the film and the substrate was estimated by the cross-cut method. The experimental parameters were: the mole fraction of MTMOS, weight fraction of silica powder, weight fraction of PET fibers, and the curing temperature. The result indicated that the contact angle and the sliding angle of the hybrid film were 153 degrees and 4 degrees, respectively, and the adhesion test result was very good (5B degree), while the mole fraction of MTMOS was 0.4, the silica powder concentration was 30 wt%, and the PET fibers concentration was 0.15 wt%, with the curing temperature in the range of 130-180 degrees C. (C) Koninklijke Brill NV, Leiden, 2011
關聯:	JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY
显示于类别:	[材料科學與工程研究所 ] 期刊論文