    题名: Deformation characteristics of fine grained magnesium alloy AZ31B thin sheet during rapid gas blow forming
    作者: Sun,PH;Wu,HY;Hsu,WC;Tsai,HH;Huang,CC;Lee,S
    贡献者: 機械工程學系
    关键词: MG ALLOY;ELEVATED-TEMPERATURES;MECHANICAL-PROPERTIES;STRETCH FORMABILITY;2-STAGE DEFORMATION;SUPERPLASTICITY;BEHAVIOR;TECHNOLOGY;CAVITATION;FLOW
    日期: 2010
    上传时间: 2012-03-27 17:02:16 (UTC+8)
    出版者: 國立中央大學
    摘要: Decreasing the forming time in gas blow forming using fine grained Mg alloy AZ31B thin sheet with a thickness of 0.6 mm was studied in this work. Tensile tests and gas blow forming using stepwise pressurisation profiles were performed to explore the deformation behaviour of a fine grained AZ31B Mg alloy sheet. The alloy sheets were successfully deformed into hemispherical domes using two proposed stepwise pressurisation profiles during gas blow forming. As a result, significant reduction in forming time was achieved. Maximum effective deformation rates of 1.02 x 10(-2) and 1.98 x 10(-2) s(-1) were obtained at 300 and 370 degrees C respectively. It was feasible to form a hemispherical dome with a height of 20 mm in less than 80 s at 370 degrees C. The results confirmed that the thickness distribution along the centreline of the formed dome was sensitive to the pressurisation profiles. A higher thinning effect was observed at 370 degrees C due to the higher deformation rate imposed during forming. Grain growth was not a serious problem for forming even at 370 degrees C, and static grain growth should be the major factor resulting in grain growth during forming.
    關聯: MATERIALS SCIENCE AND TECHNOLOGY
    显示于类别:[機械工程學系] 期刊論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    index.html0KbHTML275检视/开启


    在NCUIR中所有的数据项都受到原著作权保护.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈  - 隱私權政策聲明