Dispersion toughening of Mg-based bulk metallic glass reinforced with porous Mo particles

NCU Institutional Repository > 工學院 > 機械工程學系 > 期刊論文 > Item 987654321/50057

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/50057

題名:	Dispersion toughening of Mg-based bulk metallic glass reinforced with porous Mo particles
作者:	Jang,JSC;Ciou,JY;Li,TH;Huang,JC;Nieh,TG
貢獻者:	機械工程學系
關鍵詞:	AMORPHOUS-ALLOYS;THERMAL-STABILITY;COMPOSITES;PLASTICITY;STRENGTH
日期:	2010
上傳時間:	2012-03-27 17:02:28 (UTC+8)
出版者:	國立中央大學
摘要:	We have successfully synthesized the porous Mo particles reinforced Mg(58)Cu(28.5)Gd(11)Ag(2.5) metallic glass composites (BMGCs) rods with a diameter of 2 similar to 6 mm by injection casting in an Ar atmosphere. The glass forming ability and mechanical properties of such Mg-based BMGCs are systematically investigated as a function of porous Mo volume fraction and injection-cast cooling rate. The results show that superior mechanical performance with up to 14% compressive failure strain, 1050 MPa yield strength and 1200 MPa fracture strength at room temperature can be obtained for the Mg-based BMGC with 25 vol% Mo particles. The dispersed porous Mo particles act as a network in the amorphous matrix, which restricts the highly localized shear banding into many isolated micro-scaled regions, avoiding complete shear-through of one principal shear band across the whole sample. This results in the formation of multiple shear bands within or around the porous Mo particles and the decrease of stress concentration for further propagation of shear band, enhancing the plasticity. Moreover, the yield strength and plastic strain exhibit an increasing trend with increasing cast cooling rate, due to lower residual porosity. (C) 2009 Elsevier Ltd. All rights reserved.
關聯:	INTERMETALLICS
顯示於類別:	[機械工程學系] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
index.html		0Kb	HTML	425	檢視/開啟

在NCUIR中所有的資料項目都受到原著作權保護.

社群 sharing

資料載入中.....