English  |  正體中文  |  简体中文  |  Items with full text/Total items : 67783/67783 (100%)
Visitors : 23047345      Online Users : 204
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version

    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/50156

    Title: Strengthening and Room Temperature Age-Softening of Super-Light Mg-Li Alloys
    Authors: Leu,JS;Chiang,CT;Lee,S;Chen,YH;Chu,CL
    Contributors: 機械工程學系
    Date: 2010
    Issue Date: 2012-03-27 17:04:56 (UTC+8)
    Publisher: 國立中央大學
    Abstract: Extremely light (density similar to 1.46 g/cm(3)) and highly formable Mg-Li alloys have been drawing research interest; however, their relatively low strength is discouraging, and thus, an issue to be addressed. This paper processes and evaluates four Mg-Li alloys: the first, a basic alloy with a nominal composition of Mg-11%Li-1%Al-0.5%Zn; the second, an alloy with only Be added to the first; the third, an alloy with only Sc added to the first; and the fourth, with both Be and Sc added to the first. This research achieves a high strength of similar to 240 MPa for Mg-Li alloys using the processes of solid solution treatment plus 90% heavy rolling. A subsequent natural aging process proceeded spontaneously and resulted in strength decay. Room temperature softening behavior is uncommon, but offers a convenient route for studying age-softening characteristics of metallic alloys.
    Appears in Collections:[機械工程學系] 期刊論文

    Files in This Item:

    File Description SizeFormat

    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明