    題名: Superplastic elongation characteristic of fine grained magnesium alloy ZK60
    作者: Lee,S;Chiang,C;Leu,J;Chen,YH
    貢獻者: 機械工程學系
    關鍵詞: AA5083
    日期: 2010
    上傳時間: 2012-03-27 17:05:15 (UTC+8)
    出版者: 國立中央大學
    摘要: This paper employs simple rolling process plus annealing to refine the grain size of magnesium alloy ZK60. This goal is effectively achieved, obtaining grains as fine as similar to 3.7 mu m. Such a specimen shows an elongation of 642%, and its ultimate fracture surface exhibits intergranular separation and significant grain growth. Additionally, the effects of the specimen's geometry and tensile test axis with respect to the rolling direction on superplastic elongation is studied, which has not been done before.
    關聯: RARE METALS
    顯示於類別:[機械工程學系] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML229檢視/開啟


    在NCUIR中所有的資料項目都受到原著作權保護.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋  - 隱私權政策聲明