Dynamic strain aging in low cycle fatigue of duplex titanium alloys

NCUIR > Engineering College > Departmant of Mechanical Engineering > journal & Dissertation > Item 987654321/50212

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/50212

Title:	Dynamic strain aging in low cycle fatigue of duplex titanium alloys
Authors:	Lin,YH;Hu,KH;Kao,FH;Wang,SH;Yang,JR;Lin,CK
Contributors:	機械工程學系
Keywords:	COMMERCIALLY PURE TITANIUM;STAINLESS-STEEL;TENSILE PROPERTIES;DEFORMATION MECHANISMS;TEMPERATURE;BEHAVIOR;RATES;COMPRESSION;TI-6AL-4V;303-K
Date:	2011
Issue Date:	2012-03-27 17:06:36 (UTC+8)
Publisher:	國立中央大學
Abstract:	The influence of dynamic strain aging (DSA) on low cycle fatigue (LCF) in duplex Ti-6-4 and SP700 titanium alloys was studied. LCF was performed within the temperature range from 350 degrees C to 450 degrees C, at strain rates of 10(-3) s(-1) and 10(-4) s(-1), and strain amplitudes of 1.25% and 2%. DSA appeared as serrations at the plastic portion of the cyclic stress-strain hysteresis loop, as well as stress humps appearing in the cyclic stress response (CSR) curve of peak tensile stress response versus cycle number. Strain-induced micro twin formation was only observed in the sample after fatigue with 2% strain amplitude under a 10(-4) s(-1) strain rate, indicating that it is a DSA induced phenomenon. (C) 2011 Elsevier B.V. All rights reserved.
Relation:	MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING