Effect of Mn, Ti/Cr ratio, and heat treatment on hydrogen storage properties of TI-V-CR-MN alloys

NCU Institutional Repository > 工學院 > 機械工程學系 > 期刊論文 > Item 987654321/50213

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/50213

題名:	Effect of Mn, Ti/Cr ratio, and heat treatment on hydrogen storage properties of TI-V-CR-MN alloys
作者:	Jeng,RR;Chou,CY;Lee,SL;Wu,YC;Bor,HY
貢獻者:	機械工程學系
關鍵詞:	ABSORPTION-DESORPTION CHARACTERISTICS;SOLID-SOLUTION ALLOYS;PROTIUM ABSORPTION;BCC ALLOYS;MICROSTRUCTURE;VESSEL;FE
日期:	2011
上傳時間:	2012-03-27 17:06:37 (UTC+8)
出版者:	國立中央大學
摘要:	This study elucidates the effects of adding Mn, the Ti/Cr ratio, and high-temperature annealing on the hydrogen absorption desorption properties of Ti-V-Cr-Mn body-centered cubic alloys. The hydrogen storage properties of alloys are also modified by integrating the positive effects. X-ray diffraction analysis indicates that the lattice parameters decrease linearly with an increasing Mn content. Additionally, the reversible hydrogen desorption capacity is increased as the Mn content is increased from 0 at.% to 15 at.%, without apparently degrading hydrogen absorption capacities. Despite increasing the desorption pressure, the decrease of Ti/Cr ratio slightly reduces the absorption and desorption capacities. The Ti(33)V(33)Cr(19)Mn(15) alloy has a reversible hydrogen desorption capacity as high as 2.48 mass% at 80 degrees C. Moreover, the as-heat-treated (1200 degrees C, 10 h) Ti(31)V(33)Cr(21)Mn(15) alloy has a flatter plateau pressure and a higher amount of desorption pressure (greater than 1 atm) than those of the as-cast alloy.