    題名: Effect of trace Ce addition on the microstructures and mechanical properties of A356 (AL-7SI-0.35 Mg) aluminum alloys
    作者: Tsai,YC;Lee,SL;Lin,CK
    貢獻者: 機械工程學系
    關鍵詞: AL-SI ALLOYS;EUTECTIC MODIFICATION;CASTING ALLOYS;MISCHMETAL
    日期: 2011
    上傳時間: 2012-03-27 17:06:43 (UTC+8)
    出版者: 國立中央大學
    摘要: A356 hypoeutectic alloy is a heat-treatable Al-Si-Mg system with a normal composition of Al-7 wt.% Si and about 0.35 wt.% Mg which has seen widespread applications in the aerospace and automotive industries. The purpose of this study is to determine the influence of different amounts of Ce on the microstructures and mechanical properties of A356 alloys. The findings indicate that modification efficiency in microstructures and mechanical properties of A356 alloy are greatly enhanced by adding 1.0 wt.% Ce. Two kinds of intermetallic compounds are found in the study, including Ce-23Al-22Si and Al-17Ce-12Ti-2Si-2 Mg (in wt. %) phases. Moreover, though the ductility of the Ce modified alloys are both greatly improved, there is no positive effect on the ultimate tensile strength that can be attributed to the formation of an Al-17Ce-12Ti-25i-2 Mg phase. Furthermore, the results of thermal analysis reveal that there is no direct relationship between eutectic growth temperature and silicon morphology/modification rating.
    關聯: JOURNAL OF THE CHINESE INSTITUTE OF ENGINEERS
    顯示於類別:[機械工程學系] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML276檢視/開啟


    在NCUIR中所有的資料項目都受到原著作權保護.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋  - 隱私權政策聲明