中大機構典藏-NCU Institutional Repository-提供博碩士論文、考古題、期刊論文、研究計畫等下載:Item 987654321/50249
English  |  正體中文  |  简体中文  |  Items with full text/Total items : 78728/78728 (100%)
Visitors : 33548744      Online Users : 634
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version


    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/50249


    Title: Mechanical Properties of Copper Micrometer Pillars Fabricated by Intermittent MAGE Process
    Authors: Lin,JC;Chen,YS;Huang,CF;Yang,JH;Chang,TK;Wu,CL;Hwang,YR;Chen,TC
    Contributors: 機械工程學系
    Keywords: LOCALIZED ELECTROCHEMICAL DEPOSITION;COLUMNS;MICROFABRICATION
    Date: 2011
    Issue Date: 2012-03-27 17:07:38 (UTC+8)
    Publisher: 國立中央大學
    Abstract: A nano-universal testing machine (Nano-UTM) was used to investigate the mechanical properties of micrometer-sized copper pillars fabricated by the intermittent microanode guided electrodeposition (MAGE) process under various voltages (i.e., 2.8-3.0 V) and initial gaps (5-15 mu m) between the electrodes. The Young's modulus, yield strength, fracture strength, and strain were deduced from the testing data, and their magnitudes were determined for the experimental conditions used with MAGE. The mechanical strength was higher for micropillars that were fabricated at lower voltages with greater initial separation (e.g., with the voltage at 2.8 V and initial gap at 15 mu m) than those fabricated at higher voltages with smaller initial separation (e.g., with the voltage at 3.0 V and initial gap at 5 mu m). After examining the surface morphology and transverse microstructure, we found that the stronger pillars revealed a smooth appearance with a dense internal microstructure, whereas the weaker pillars revealed a rough appearance with a porous internal microstructure. The fracture morphology was investigated to clarify the failure mechanism for various micrometer-sized copper pillars fabricated using the same MAGE process but under different conditions.
    Relation: INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE
    Appears in Collections:[Departmant of Mechanical Engineering ] journal & Dissertation

    Files in This Item:

    File Description SizeFormat
    index.html0KbHTML583View/Open


    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 隱私權政策聲明