Highly conductive alumina-added ZnO ceramic target prepared by reduction sintering and its effects on the properties of deposited thin films by direct current magnetron sputtering

NCU Institutional Repository > 資訊電機學院 > 電機工程學系 > 期刊論文 > Item 987654321/51957

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/51957

题名:	Highly conductive alumina-added ZnO ceramic target prepared by reduction sintering and its effects on the properties of deposited thin films by direct current magnetron sputtering
作者:	Huang,HS;Tung,HC;Chiu,CH;Hong,IT;Chen,RZ;Chang,JT;Lin,HK
贡献者:	電機工程學系
关键词:	AL-DOPED ZNO;ZINC-OXIDE FILMS;ELECTRICAL-PROPERTIES;SOLAR-CELLS;TEMPERATURE
日期:	2010
上传时间:	2012-03-28 10:11:50 (UTC+8)
出版者:	國立中央大學
摘要:	To obtain a suitable sputtering target for depositing transparent conducting Al-doped ZnO (AZO) films by using direct current (DC) magnetron sputtering, this study investigates the possibility of using atmosphere controlled sintering of Al(2)O(3) mixed ZnO powders to prepare highly conductive ceramic AZO targets Experimental results show that a gas mixture of Ar and CO could produce a sintered target with resistivity in the range of 2.23 x 10(-4) Omega cm. The fairly low resistivity was mainly achieved by the formation of both aluminum substitution (Al(Zn)) and oxygen vacancy (V(O)). thus greatly increasing the carrier concentration. Compared to usual air sintered target, the thin film deposited by the Ar + CO sintered target exhibited lower film resistivity and more uniform spatial distribution of resistivity A film resistivity as low as 6.8 x 10(-4) Omega cm was obtained under the sputtering conditions of this study. ((C) 2010 Elsevier B.V. All rights reserved.