Mn對含鐵A356鑄造鋁合金機械性質之影響;Effects of Mn on mechanical properties of A356 alloys containing Fe

NCUIR > Engineering College > Graduate Institute of Mechanical Engineering > Electronic Thesis & Dissertation > Item 987654321/53954

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/53954

Title:	Mn對含鐵A356鑄造鋁合金機械性質之影響;Effects of Mn on mechanical properties of A356 alloys containing Fe
Authors:	徐啓富;Hsu,Chi-Fu
Contributors:	機械工程研究所
Keywords:	A356合金;富鐵相;機械性質;A356 alloys;Iron intermetallic;Mechanical proper
Date:	2012-08-22
Issue Date:	2012-09-11 18:19:55 (UTC+8)
Publisher:	國立中央大學
Abstract:	A356鋁合金為一可熱處理型鑄造鋁合金，因其具有良好之流動性、磨耗性與焊接性等優點，已被廣泛應用於航空與汽車工業，然而A356鋁合金中的鐵元素，易與鋁形成β-Al_5 FeSi針狀富鐵相，造成合金機械性質的傷害。本研究藉由微結構觀察與機械性質試驗，探討不同含量的鐵與錳元素對A356鑄鋁合金(Al-7Si-0.3Mg)機械性質之影響。分別以光學顯微鏡(OM)、電子微探儀(EPMA)及掃描式電子顯微鏡(SEM)，觀察合金中的微結構變化與破裂斷面。結果顯示合金中的共晶矽含量與形態，並未因鐵與錳的添加而有差異。而針狀β-Al_5 FeSi富鐵相隨鐵含量的增加而增多且粗大化，導致合金機械性質、尤其是延性的顯著損害。另外錳的添加，可使針狀β-Al_5 FeSi富鐵相轉變為多邊型α-Al15(Fe,Mn)3Si2富鐵相，可有效改善合金機械性質、提升延性。此外，合金中鐵含量愈高，所需添加之錳含量亦須提高，才能達到改善效果。A356　aluminum　alloy　is　a　heat　treatment　type　cast aluminum　alloy,　with　excellent　casting　characteristics、resistance　to　corrosion　and　good weldability,　have　been　widely　used　in　aircraft　and automotive　industry.Iron　is　the　most　common　and　harmful　impurity　in A356　aluminium　alloys　forming　acicular　form　of　β-Al5FeSi　iron　intermetallic　phase,　which　is　detrimental　to the　mechanical　properties. In　this　study,　the　effect　of　Mn　and　Fe　on mechanical　properties　of　A356　alloys　by　used microstructure　observed(OM、EPMA and SEM)　and　mechanical test. Addition　of　Fe　and　Mn　elements　has　no　obviously influence　on　the　type　and　amount　of　eutectic　silicon　in　A356　alloy.　Increasement　of　Fe　content　in　A356 alloy,　which　amount　and　size　increase　with　increasing　Fe　content.　And　lead　to　the　decline　of　mechanical properties.　Addition　of　Mn　change　the　morphology　of β-Al5FeSi　acicular　iron　intermetallic　phase　to　α-Al15(Fe,Mn)3Si12　polyhedral　form　leading　to　significant　improvement　in　mechanical　properties.
Appears in Collections:	[Graduate Institute of Mechanical Engineering] Electronic Thesis & Dissertation

Files in This Item:

File	Description	Size	Format
index.html		0Kb	HTML	672	View/Open

社群 sharing

Loading...